Corrosion behavior and surface characterization of Ti-20Cr alloy in a solution containing fluoride.
نویسندگان
چکیده
The purpose of this study was to investigate the correlation between corrosion resistance and surface composition of an experimental Ti-20 mass% Cr casting alloy in a saline solution containing fluoride. The alloy had a greater resistance to corrosion in a fluoride-containing saline solution than did commercially pure titanium. However, with confirmed dissolution of titanium and chromium, it meant that the fluoride in the saline solution corroded the alloy slightly. X-ray photoelectron spectroscopy analysis revealed that the surface composition of the alloy consisted of titanium and chromium oxides containing hydroxide. The [Ti]/([Ti] + [Cr]) ratio in the surface oxide film decreased when immersed in fluoride-containing saline solution, that is, the surface oxide film became chromium-rich oxide. Therefore, the alloy obtained good corrosion resistance to fluoride due to formation of a chromium-rich oxide film.
منابع مشابه
Fretting Corrosion Behavior of Experimental Ti-20Cr Compared to Titanium
Experimental cast titanium alloys containing 20 mass% chromium (Ti-20Cr) show preferable mechanical properties and a good corrosion resistance. This study evaluated the fretting corrosion behavior of Ti-20Cr. Ti-20Cr (n = 4) and commercially pure titanium (CP-Ti, n = 6) disk specimens were used. The fretting corrosion test was performed by electrochemical corrosion at 0.3 V in 0.9% saline solut...
متن کاملCorrosion behavior of pure titanium and titanium alloys in fluoride-containing solutions.
The effects of fluoride concentrations and pH on the corrosion behavior of pure titanium, Ti-6Al-4V, Ti-6Al-7Nb alloys and a new Ti alloy adding palladium, which is expected to promote a repassivation of Ti were examined by anodic polarization and corrosion potential measurements. The amount of dissolved Ti was analyzed by inductively coupled plasma mass spectroscopy. The surface of the specime...
متن کاملDiscoloration of Ti-20Cr alloy in oral environment and its surface characterization.
The objective of this study was to evaluate change in color in experimental titanium-20mass% chromium (Ti-20Cr) alloy in an oral environment. Pure Ti and Ti-6Al-7Nb and Co-29Cr-5Mo alloys, as references to compare change in color, were prepared by casting. The cast specimen was mirror-polished. Each specimen was affixed to a palatal plate and the plate then worn by a volunteer for up to 300 h. ...
متن کاملThe effect of fluoride-containing oral rinses on the corrosion resistance of titanium alloy (Ti-6Al-4V)
OBJECTIVE The purpose of this study was to examine the effect of commercially available fluoride-containing oral rinses on the corrosion behavior of titanium alloys, which are the main components of orthodontic miniscrews. METHODS Four commercially available oral rinses (solution A, pH 4.46/260 ppm fluoride; solution B, pH 4.41/178 ppm fluoride; solution C, pH 6.30/117 ppm fluoride; and solut...
متن کاملDiscoloration and Dissolution of Titanium Peroxide - or Fluoride - containing Solutionsand Titanium Alloys withImmersion in
fluoride-containing solutien. Commercially pure titanium (CP-Ti) and six titanium-based alloys were used: Ti-O.15Pd, Ti6Al-4V, Ti-7Nb-6Al, Ti-55Ni, Ti-10Cu, and Ti-20Cr. Two test solutions were prepared fbr immersion of polished titanium and titanium alloys: one consisting of O,2% NaF + O,9% NaCl (pH 3.8 with lactic acid) and the other of O.1 mol/1 H202 + O.9% NaCl (pH 5.5). Following immersion...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Dental materials journal
دوره 23 3 شماره
صفحات -
تاریخ انتشار 2004