Luminescence properties and energy transfer in Tb3+ and Eu3+ co-doped Ba2P2O7 phosphors

The Ba2P2O7:Tb , Eu phosphors were synthesized by a high temperature solid-state reaction method in air atmosphere and their crystal structures, lifetime, luminescence properties, and energy transfer mechanism were investigated in detail. A series of characteristic emissions of Ba2P2O7:Tb , Eu phosphors were observed in the emission spectra at around 545 nm, 593 nm, and 613 nm when excited at 378 nm. The energy-transfer mechanism from Tb to Eu in Ba2P2O7 is determined by a dipole– dipole interaction. The emission intensity of Ba2 xP2O7:xEu 3+ was enhanced by doping charge compensation Li, Na and K. The CIE coordinates of the phosphors can be tuned from blue-green through white, to yellow and finally to orange-red with changing the Eu/Tb ratio. The average decay time of Eu increases from 2.10 to 5.81 ms with the concentration of Tb increasing from 2% to 8%, and reaches the maximum at 0.08, and is shortened when the concentration of Tb goes beyond 8%.