Effect of triple junctions on deformation twinning in a nanostructured Cu–Zn alloy: A statistical study using transmission Kikuchi diffraction
نویسندگان
چکیده
Scanning electron microscopy transmission Kikuchi diffraction is able to identify twins in nanocrystalline material, regardless of their crystallographic orientation. In this study, it was employed to characterize deformation twins in Cu/10 wt % Zn processed by high-pressure torsion. It was found that in 83% of grains containing twins, at least one twin intersects with a triple junction. This suggests that triple junctions could have promoted the nucleation of deformation twins. It should be cautioned that this technique might be unable to detect extremely small nanoscale twins thinner than its step size.
منابع مشابه
The effect of twinning on texture evolution during ECAP processing of an AM30 magnesium alloy
An AM30 magnesium alloy was processed through ECAP method at 200 °C. Optical and transmission electron microscopy as well as electron back scattered diffraction (EBSD) technique were employed to characterize the deformed microstructure. A partially recrystallized microstructure including ultrafine/nano structures was obtained. The area fraction of 49% was measured for the recrystallized regions...
متن کاملDeformation twinning induced decomposition of lamellar LPSO structure and its re-precipitation in an Mg-Zn-Y alloy
The high hardness or yield strength of an alloy is known to benefit from the presence of small-scale precipitation, whose hardening effect is extensively applied in various engineering materials. Stability of the precipitates is of critical importance in maintaining the high performance of a material under mechanical loading. The long period stacking ordered (LPSO) structures play an important ...
متن کاملStudy on the Microstructure of Hot Deformed Cu-28Zn Prealloyed Powder Compacts
The role of microstructure on hot deformation behavior of sintered Cu-28Zn prealloyed powder compacts was investigated by a series of isothermal hot compression tests in the temperature range of 550- 850°C at strain rates of 0.001, 0.01, 0.1 and 0.5 s-1, by taking into consideration the Hyperbolic Sine functional behavior to analyze the deformation behavior of the alloy. The results indicate th...
متن کاملNanotwins Formation in Accumulative Roll-Bonded Brass
Accumulative roll-bonding (ARB) is a severe plastic deformation process that is using rolling to produce ultrafine grains in coarse grained metallic materials. In this study, ARB has been applied on 70/30 brass up to 6 cycles at ambient temperature and non-lubricated conditions to apply a true strain up to 4.8 Von Mises strain. Microstructures of ARBed brass samples were characterized by scanni...
متن کاملInvestigation of early stage deformation mechanisms in a metastable β titanium alloy showing combined TWIP and TRIP effects
As expected from the alloy design procedure, combined Twinning Induced Plasticity (TWIP) and Transformation Induced Plasticity (TRIP) effects are activated in a metastable β Ti-12(wt.%)Mo alloy. In-situ Synchrotron X-ray diffraction (XRD), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) observations were carried out to investigate the deformation mechanisms an...
متن کامل