Nanoporous carbons through direct carbonization of a zeolitic imidazolate framework for supercapacitor electrodes.
نویسندگان
چکیده
Nanoporous carbons with high surface area are achieved through direct carbonization of a commercially available zeolitic imidazolate framework (ZIF-8) without any additional carbon sources. The resultant nanoporous carbons exhibit high electrochemical capacitances in an acidic aqueous electrolyte.
منابع مشابه
Porous Proton Exchange Membrane Based Zeolitic Imidazolate Framework-8 (ZIF-8)
Metal-organic frameworks (MOFs) are emerging material class for the past few years due to its tailorability characteristics for various applications. However, the research and development (R&D) of MOFs is still scarce for fuel cell system. This may be due to the several difficulties faced in selecting a good MOFs-based electrolyte, which consequently affects both proton conduction and methanol ...
متن کاملControlling porosity in lignin-derived nanoporous carbon for supercapacitor applications.
Low-cost renewable lignin has been used as a precursor to produce porous carbons. However, to date, it has not been easy to obtain high surface area porous carbon without activation processes or templating agents. Here, we demonstrate that low molecular weight lignin yields highly porous carbon with more graphitization through direct carbonization without additional activation processes or temp...
متن کاملMetal–organic framework (MOF) as a template for syntheses of nanoporous carbons as electrode materials for supercapacitor
Five nanoporous carbons (NPCs) were prepared by polymerizing and then carbonizing carbon precursor of furfuryl alcohol accommodated in a porous metal–organic framework (MOF-5, [Zn4O(bdc)3], bdc = 1,4-benzenedicarboxylate) template. The Brunauer–Emmett– Teller (BET) surface areas for five NPC samples obtained by carbonizing at the temperatures from 530 to 1000 C fall into the range from 1140 to ...
متن کاملZIF-Derived Nitrogen-Doped Porous Carbons for Xe Adsorption and Separation
Currently, finding high capacity adsorbents with large selectivity to capture Xe is still a great challenge. In this work, nitrogen-doped porous carbons were prepared by programmable temperature carbonization of zeolitic imidazolate framework-8 (ZIF-8) and ZIF-8/xylitol composite precursors and the resultant samples are marked as Carbon-Z and Carbon-ZX, respectively. Further adsorption measurem...
متن کاملMechanochemical dry conversion of zinc oxide to zeolitic imidazolate framework.
Mechanochemical dry conversion that only uses zinc oxide and an imidazole ligand proved to be effective and reliable for fabrication of a zeolitic imidazolate framework with a polycrystalline grain boundary and a core-shell structure. The zinc oxide crystals are converted into a zeolitic imidazolate framework to a depth of approx. 10 nm below the surface.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 48 58 شماره
صفحات -
تاریخ انتشار 2012