Prediction of post overload fatigue crack growth life of HSLA steel under mixed-mode (I and II) spike overload by using genetic programming
نویسنده
چکیده
In the present investigation, fatigue crack growth tests under mixed-mode (I and II) overload have been conducted on HSLA steel and subsequently genetic programming has been applied to predict post overload fatigue life. It is observed that the proposed model predicts fatigue life of HSLA steel with reasonable accuracy.
منابع مشابه
Application of a strip-yield model to predict crack growth under variable-amplitude and spectrum loading – Part 1: Compact specimens
Fatigue-crack-growth tests were conducted on compact, C(T), specimens made of D16Cz (clad) aluminum alloy under constant-amplitude loading, a single spike overload, and simulated aircraft spectrum loading. Constant-amplitude tests were conducted to generate crack-growth-rate data from threshold to near fracture over a wide range of stress ratios (R = Pmin/Pmax = 0.1–0.75) using the new compress...
متن کاملCrack Behavior of the Aluminum Alloy 2024 Under Fretting Conditions
The initial stage of fretting fatigue crack growth is significantly influenced by tangential force induced by fretting action along the contact surface where a mixed-mode crack growth is involved. Fretting crack behavior of aluminum alloy 2024 was studied, taking into account the problem of contact asperities. Finite element was used for the determination of the stress field near the contact su...
متن کاملFracture mechanics-based life prediction of a riveted lap joint
In this paper, three-dimensional modeling of the fatigue crack growth profiles was performed in a simple riveted lap joint. Simulation results showed that mode I was dominated on the one side of the plates and the crack straightly grew on this side, while the other side of the plates was in a mixed-mode condition and the crack propagation path was not straight on this side. Afterward, the fract...
متن کاملPrediction of mode-I overload-induced fatigue crack growth rates using neuro-fuzzy approach
This is the pre-peer reviewed version of the article: Mohanty J R, Verma B B, Ray P K, Parhi D R K, Prediction of mode-I overload-induced fatigue crack growth rates using neuro-fuzzy approach, Expert Systems with Applications, 37(2010), 3075-3087, which has been published in the final form at http://www.sciencedirect.com/science/journal/09574174 Prediction of mode-I overload-induced fatigue cra...
متن کاملModeling of Corrosion-Fatigue Crack Growth Rate Based on Least Square Support Vector Machine Technique
Understanding crack growth behavior in engineering components subjected to cyclic fatigue loadings is necessary for design and maintenance purpose. Fatigue crack growth (FCG) rate strongly depends on the applied loading characteristics in a nonlinear manner, and when the mechanical loadings combine with environmental attacks, this dependency will be more complicated. Since, the experimental inv...
متن کامل