Rheological and Performance Research on a Regenerable Polyvinyl Alcohol Fracturing Fluid.
نویسندگان
چکیده
A regenerable polyvinyl alcohol/organic boron fracturing fluid system with 1.6 wt% polyvinyl alcohol (PVOH) and 1.2 wt% organic boron (OBT) was studied, and its main regeneration mechanism is the reversible cross-linking reaction between B(OH)4- and hydroxyl groups of PVOH as the change of pH. Results of rheology evaluations show that both the apparent viscosity and the thermal stability of the fracturing fluid decreased with the regeneration number of times increasing. In addition, the apparent viscosity of the fluid which was without regeneration was more sensitive to the shear action compared with that of the fluid with regeneration once or twice. When the fracturing fluid was without regeneration, the elasticity was dominating due to the three-dimensional network structure of the formed gel; the viscosity gradually occupied the advantage when the fracturing fluid was regenerated once or twice. The settling velocity of proppant was accelerated by both the regeneration process and the increasing temperature, but it was decelerated when the proppant ratio increased. Results of core damage tests indicate that less permeability damage was caused by the PVOH/OBT fracturing fluid compared with that caused by the guar gum fracturing fluid after gel breaking.
منابع مشابه
Novel Kefiran-Polyvinyl Alcohol Composite Film: Physical, Mechanical and Rheological Properties
Background and Objectives: Kefiran (Kef) is a water-soluble polysaccharide that can form transparent film however, it is brittle. Therefore, in order to improve the mechanical properties of kefiran film, a mixture with other polymers can be offered. The expansion of mixed systems can propose kefiran and polyvinyl alcohol (PVOH) as a new composite film. Materials and Methods: Solutions of 20 gr...
متن کاملMaximizing Performance of the Membranes Based on Quaternized Polysulfone/Polyvinil Alcohol for Biomedical Applications: Rheological Investigations
The rheological response of blends obtained from quaternized polysulfone and polyvinyl alcohol in N-methyl-2pyrrolidone as against structural peculiarity of polymers from the blend, composition of polymer mixtures, as well as the types of interactions were investigated. Results show that the variation of polyvinyl alcohol composition in the studied system determines changes of the rheological p...
متن کاملEFFECT OF OPERATING CONDITIONS ON THE DEHYDRATION OF TOLUENE BY PERVAPORATION USING A POLYVINYL ALCOHOL MEMBRANE
The effects of operating parameters such as feed temperature and permeate-side pressure on the performance of a commercial PVA membrane in the dehydration of toluene by a pervaporation (PV) membrane system is studied in the present work. The results obtained indicate that increasing temperature in the range of 40 to 70 °C and reducing permeate pressure in the range of 1 to 10 mmHg increase memb...
متن کاملFabrication of Polyvinyl Alcohol/Kefiran Nanofibers Membrane Using Electrospinning
The Poly (vinyl alcohol)/Kefirane nanofiber membrane was successfully fabricated for the firsttime using electrospinning of the polyvinyl alcohol (PVA) and Kefirane blend solution. Scanningelectron microscope (SEM), attenuated total reflectance Fourier transform infrared (ATRFT-IR), and differential scanning calorimetry (DSC) were used to characterize the electrospunPoly (vinyl alcohol)/Kefiran...
متن کاملThe Effect of Adding Alginate Natural Polymer on the Structure of Polyvinyl Alcohol Biocompatible Nanofibers in Electrospinning Process
Background: Nowadays, in order to preserve the environment and sustainable development, the use of natural and renewable resources is a priority for industries. High performance and specific structure of nano-biocompatible materials has attracted researchers. In this research, alginate polymer, which is generally obtained from marine sources such as algae, was added to polyvinyl alcohol nanofi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- PloS one
دوره 10 12 شماره
صفحات -
تاریخ انتشار 2015