Glass ionomer layer thickness and its influence on zirconia failure.

نویسندگان

  • Michael Behr
  • Sebastian Meier
  • Sebastian Hahnel
  • Ralf Bürgers
  • Gerhard Handel
  • Martin Rosentritt
چکیده

OBJECTIVES To investigate the influence of glass ionomer cement layers with various thickness and cement contamination on the fracture resistance of thin zirconia plates luted onto coplanar human molars. MATERIALS AND METHODS Zirconia plates measuring 0.7 mm in thickness were luted onto 70 coplanarly trimmed human molars with glass ionomer cement. Cement layers measuring 100, 250, 1000, and 2000 μm in thickness were produced. Contamination of the tooth surface was achieved by applying hand-piece oil, contamination of the cement by mixing glass ionomer with H(2)O(2) to produce voids and gas bubbles. RESULTS Fracture resistance was independent from cement layer thickness (median ranging from 1220 to 1367 N). Oil contamination moderately reduced fracture resistance (1135 N). Fracture resistance was significantly affected by the presence of a considerable amount of voids or gas bubbles in the cement (877 N). CONCLUSIONS The fracture resistance of thin zirconia plates was not affected by different cement layer thickness but by contamination of the tooth surface as well as by high cement porosity due to simulated handling errors.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effects of N-Vinylcaprolactam Containing Polyacids and Zirconia on Mechanical Properties of Commercial Glass Ionomer Cements

 This study aimed to investigate the impact of N-vinylcaprolactam (NVC) and Nano-sized yttria-stabilized zirconia (YSZ), separately and simultaneously, on the mechanical properties of the commercial glass ionomer cements (GICs). Methods: The NVC is able to ameliorate the mechanical and surface properties of glass ionomers; however, its effect hasn’t been investigated in conjunc...

متن کامل

Biomechanical three-dimensional finite element analysis of monolithic zirconia crown with different cement type

PURPOSE The objective of this study was to evaluate the influence of various cement types on the stress distribution in monolithic zirconia crowns under maximum bite force using the finite element analysis. MATERIALS AND METHODS The models of the prepared #46 crown (deep chamfer margin) were scanned and solid models composed of the monolithic zirconia crown, cement layer, and prepared tooth w...

متن کامل

بررسی اثرکامپوزیت Light Cure و کامپوزیت Self Cure بر باندگلاس آینومر نوری به عاج دندان (In-vitro)

Statement of Problem: Composite reins have recently become popular for posterior teeth restorations. Gap formation and subsequent microleakage are of the complications resulting from such restorations. One of the techniques to overcome polymerization shrinkage of composite resins is sandwich technique (application of glass ionomer as a base beneath the composite resin). Since polymerization pat...

متن کامل

Effect of Zirconia and Alumina Fillers on the Microstructure and Mechanical Strength of Dental Glass Ionomer Cements.

BACKGROUND Glass-ionomer cements perform a protective effect on the dentin-pulp complex considering the F ions release and chemical bonding to the dental structures. On the other hand, those materials have poor physic-mechanical properties in comparison with the restorative resin composite. The main aim of this work was to evaluate the influence of zirconia and/or alumina fillers on the microst...

متن کامل

Effect of cement type on the color attributes of a zirconia ceramic

PURPOSE This in vitro study evaluated the effects of four different cements on the color attributes of a zirconia ceramic. MATERIALS AND METHODS 40 zirconia ceramic disk specimens (0.5 mm thickness, 10 mm diameter, 0.1 mm cement space) were fabricated by a computer-aided design and computer-aided manufacturing system. The specimens were divided into 4 groups of 10 specimens and cemented to co...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Journal of the mechanical behavior of biomedical materials

دوره 4 7  شماره 

صفحات  -

تاریخ انتشار 2011