Anomalous Structure of Palladium-Capped Magnesium Thin Films
نویسنده
چکیده
Pd capped pure Mg thin film (50 nm thick) was prepared by magnetron sputtering and its hydrogenation at room temperature has been investigated. After exposure to 4% hydrogen gas diluted by argon, the Pd/Mg thin films show drastic optical changes from the metallic state to the transparent state within five seconds by hydrogenation. Transmission electron microscope observation reveals that this sample has an anomalous structure; Mg grain is surrounded by Pd. This structure may be the reason why Pd/Mg films can be hydrogenated so quickly at room temperature.
منابع مشابه
Study of Composition and Optical Properties of Chemically Deposited Pd-xSb2S3 Thin Films
The study reports on the effects of different concentration of palladium impurities on the compositional and optical properties of Palladium Doped Antimony Sulphide (Pd-xSb2S3) thin films grown by the chemical bath deposition method. The films were grown at room temperature and other deposition conditions such as the bath temperature, pH, complexing agents were kept constant. The concentration ...
متن کاملOPTICAL PROPERTIES OF THIN Cu FILMS AS A FUNCTION OF SUBSTRATE TEMPERATURE
Copper films (250 nm) deposited on glass substrates, at different substrate temperatures. Their optical properties were measured by ellipsometery (single wavelength of 589.3 nm) and spectrophotometery in the spectral range of 200–2600 nm. Kramers Kronig method was used for the analysis of the reflectivity curves of Cu films to obtain the optical constants of the films, while ellipsometery measu...
متن کاملLong-term stability of capped and buffered palladium-nickel thin films and nanostructures for plasmonic hydrogen sensing applications
One of the main challenges in optical hydrogen sensing is the stability of the sensor material. We found and studied an optimized material combination for fast and reliable optical palladium-based hydrogen sensing devices. It consists of a palladium-nickel alloy that is buffered by calcium fluoride and capped with a very thin layer of platinum. Our system shows response times below 10 s and alm...
متن کاملHydrogen gas sensing properties of PdO thin films with nano-sized cracks.
We report on a novel method for the fabrication of highly sensitive hydrogen gas sensors based on palladium oxide thin films and have investigated their hydrogen sensing properties and nanostructures. To our knowledge, this is the first report on the use of palladium oxide and reduced palladium thin films as hydrogen sensors. The palladium oxide thin films were deposited on thermally oxidized S...
متن کاملNano-structural Characterization of Post-annealed ZnO Thin Films by X-ray Diffraction and Field Emission Scanning Electron Microscopy
ZnO thin films were deposited on Si(400) substrates by e-beam evaporation technique, and then post-annealed at different annealing temperatures (200-800°C). Dependence of the crystallographic structure, nano-strain, chemical composition and surface physical Morphology of these layers on annealing temperature were studied. The crystallographic structure of films was studied using X-Ray Diffracti...
متن کامل