photocatalytic degradation of triton x-100 by zinc oxide nanoparticles
نویسندگان
چکیده
in this study the application of zno nanoparticles to uv photocatalytic degradation of nonionic surfactanttriton x-100 in aqueous media was investigated. the affecting factors on the photodegradation such as tritonx-100 initial concentration, nanocatalyst weight, ph, temperature and other parameters were studied anddescribed in details. the degradation rate was found to be strongly influenced by all the above parameters .theoptimized conditions for maximum amount of degradation were also determined results showed that thephotocatalytic degradation process using uv light as an irradiation source, and nanoparticles of zno as aphotocatalyst, was applicable for the degradation of triton x-100 in aqueous solution and wastewater samples.
منابع مشابه
Photocatalytic Degradation of Triton X-100 by Zinc oxide Nanoparticles
In this study the application of ZnO nanoparticles to UV photocatalytic degradation of nonionic surfactantTriton X-100 in aqueous media was investigated. The affecting factors on the photodegradation such as TritonX-100 initial concentration, nanocatalyst weight, pH, temperature and other parameters were studied anddescribed in details. The degradation rate was found to be strongly influenced b...
متن کاملphotocatalytic degradation of Triton X-100 in aqueous phase with Zinc oxide as a nanoparticle under UV light irradiation
The photocatalytic degradation of nonionic surfactant Triton X-100 was studied by a batch process using ZnOcommercial powders as the catalyst on irradiation with UV light and its behaviour comparatively with respect toZnO nanoparticles with diameter size 20 nm. The effects of different conditions such as catalyst type, amount ofthe photocatalyst, pH of the system, initial concentration and elec...
متن کاملphotocatalytic degradation of triton x-100 in aqueous phase with zinc oxide as a nanoparticle under uv light irradiation
the photocatalytic degradation of nonionic surfactant triton x-100 was studied by a batch process using znocommercial powders as the catalyst on irradiation with uv light and its behaviour comparatively with respect tozno nanoparticles with diameter size 20 nm. the effects of different conditions such as catalyst type, amount ofthe photocatalyst, ph of the system, initial concentration and elec...
متن کاملPhotocatalytic dye degradation properties of Zinc Copper Ferrites nanoparticles
In the present study, new multi-components spinel ferrite Zinc doped metallic ferrites are investigated. The synthesized compounds consisting of Zinc copper ferrite nanostructures were developed using the Co-precipitation technique. Powder X-ray diffraction pattern (XRD) confirms the formation of the spinel phase for all the samples. The lattice constant was studied through powder X-ray diffrac...
متن کاملElectrocatalytic oxidation of formaldehyde onto Pt nanoparticles modified poly (m-toluidine)/Triton X-100 film
In this work, spherical Pt nanometer-scale particles supported on the poly (m-toluidine)/Triton X-100 film modified carbon nanotube paste electrode (Pt/PMT (TX-100)/MCNTPE) was used as a potent catalyst for electrooxidation of formaldehyde (HCHO) in both 0.5 M H2SO4 and 0.1 M NaOH solutions. The obtained results showed that utilization of TX-100 as an additive during the electropolymerization p...
متن کاملRapid degradation of zinc oxide nanoparticles by phosphate ions
Zinc oxide nanoparticles are highly sensitive towards phosphate ions even at pH 7. Buffer solutions and cell culture media containing phosphate ions are able to destroy ZnO nanoparticles within a time span from less than one hour to one day. The driving force of the reaction is the formation of zinc phosphate of very low solubility. The morphology of the zinc oxide particles has only a minor in...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
journal of physical & theoretical chemistryISSN
دوره 7
شماره 3 2010
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023