kinethical aspects of high solid contents copoly(styrene/butylacrylate)-cloisite 30b nanocomposites

نویسندگان

m. mirzataheri

چکیده

high solid content poly (styrene-co-butyl acrylate) latex ( with 20% and 40% solid content) including high amounts of cloisite 30b (7 wt% and 10 wt%) were kinetically investigated. gravimetric method via measuring the rate of polymerization, number of particles and average number of radicals per particle was used. results showed that by increasing the solid content; the average diameter of polymer particles decreased. studies on the polymerization rate depict that the increase in polymer particle size provides more average reactive radicals per polymer particle, which increased from 0.48 to 0.88 for the sample containing 7 wt% clay and 20 wt% solid content. observed armored particles with honeycomb morphology is the most novelty of this research work, which is suitable for making barrier packaging films.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Kinethical Aspects of High Solid Contents Copoly(Styrene/Butylacrylate)-Cloisite 30B Nanocomposites

High solid content poly (styrene-co-butyl acrylate) latex ( with 20% and 40% solid content) including high amounts of Cloisite 30B (7 wt% and 10 wt%) were kinetically investigated. Gravimetric method via measuring the rate of polymerization, number of particles and average number of radicals per particle was used. Results showed that by increasing the solid content; the average diameter of poly...

متن کامل

High Solid Contents Copoly (Styrene/Butyl Acrylate)-Cloisite 30B Nanocomposites

Higher solid contents (20 % and 40 %) nanocomposites of poly (styrene-co-butyl acrylate) including higher content of Cloisite 30B (7 wt% and 10 wt %) were prepared via miniemulsion polymerization. Stability of the final latexes proved outstanding combination of polymerization procedure and surfactants. Morphological studies revealed by TEM, SAX and XRD showed three structures of core-shell, arm...

متن کامل

high solid contents copoly (styrene/butyl acrylate)-cloisite 30b nanocomposites

higher solid contents (20 % and 40 %) nanocomposites of poly (styrene-co-butyl acrylate) including higher content of cloisite 30b (7 wt% and 10 wt %) were prepared via miniemulsion polymerization. stability of the final latexes proved outstanding combination of polymerization procedure and surfactants. morphological studies revealed by tem, sax and xrd showed three structures of core-shell, arm...

متن کامل

Synthesis and characterization of linear polylactic acid-based urethanes using Tin modified solid cloisite-30B catalyst

In recent year, biocompatible, biodegradable materials (linear polylactic acid-based urethanes) in the solid and/or liquid form have attracted tremendous attention in biomedical application particularly in stent coating. Low molecular weight poly (lactic acid) s (PLA), having narrow molecular weight distribution was by dehydropolycondensation method using tetraphenyltin as a catalyst. Hydroxyl ...

متن کامل

Synthesis and Characterization of Sunflower Oil-Based Polysulfide Polymer/Cloisite 30B Nanocomposites

In current work, halogenated sunflower oil was reacted with Na2S3 to produce sunflower oil-based polysulfide polymer. Cloisite 30B as organomodified nanoclay was used in different contents to investigate its effect on the properties of the synthesized polymer. All nanocomposites were prepared via in situ polymerization method in aqueous media. Fourier Transform-InfraRe...

متن کامل

Investigating the effects of chemical modification of clay nanoparticles on thermal degradation and mechanical properties of TPU/nanoclay composites

Thermoplastic polyurethane (TPU)/clay nanocomposites were prepared via a melt-compounding method using ester type TPU and two different modified organoclays (Cloisite 30B and Cloisite 15A) in different contents. The Effects of the chemical structure and content of the nanoclays on the thermal degradation and mechanical properties of TPU were also investigated. The effect of structural modificat...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
journal of nanostructures

ناشر: university of kashan

ISSN 2251-7871

دوره 4

شماره 1 2014

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023