effect of bacterial lipopolysaccharide contamination on gutta percha- versus resilon-induced human monocyte cell line toxicity.
نویسندگان
چکیده
cytotoxic effects of obturation materials were tested in presence and absence of endotoxin on human monocytes in vitro.human monocytes from thp-1 cell line were cultured. three millimeters from the tip of each resilon and gutta percha points were cut and directly placed at the bottom of the culture wells. cultured cells were exposed to gutta percha (groups g1 and g2) and resilon (r1 and r2). ten μg/ml bacterial lipopolysaccharide (lps) was added to the culture wells in groups g1 and r1. positive control included the bacterial lps without the root canal filling material and the negative control contained the cells in culture medium only. viability of cells was tested in all groups after 24, 48, and 72 hours using the methylthiazolyldiphenyl-tetrazolium bromide (mtt) assay for at least 3 times to obtain reproducible results. optical density values were read and the data were analyzed using three-way anova and post hoc statistical test.the results showed that cells in g2 had the lowest rate of viability at 24 hours, but the lowest rate of viable cells was recorded in g1 at 48 and 72 hours. the effect of lps treatment was not statistically significant. resilon groups showed cell viability values higher than those of gutta percha groups, although statistically non-significant (p=0.105). cell viability values were lower in gutta percha than resilon groups when lps-treated and lps-untreated groups were compared independently at each time point.it could be concluded that none of the tested root canal filling materials had toxic effects on cultured human monocyte cells whether in presence or absence of lps contamination.
منابع مشابه
Effect of Bacterial Lipopolysaccharide Contamination on Gutta Percha- versus Resilon-Induced Human Monocyte Cell Line Toxicity
OBJECTIVES Cytotoxic effects of obturation materials were tested in presence and absence of endotoxin on human monocytes in vitro. MATERIALS AND METHODS Human monocytes from THP-1 cell line were cultured. Three millimeters from the tip of each Resilon and gutta percha points were cut and directly placed at the bottom of the culture wells. Cultured cells were exposed to gutta percha (groups G1...
متن کاملComparison between gutta-percha and Resilon retreatment.
Retreatment procedures in endodontic practice require complete removal of the original root filling materials. The aim of this study was to compare the amount of residual filling material on the walls of root canals that were obturated with gutta-percha or Resilon. Thirty extracted single-rooted human teeth were selected and instrumented by RaCe rotary instruments up to MAF #35. They were rando...
متن کاملSolvent capacity of different substances on gutta-percha and Resilon.
The aim of this study was to evaluate the effectiveness of 3 solvents (eucalyptol, orange oil, and xylol) on 2 types of gutta-percha (conventional and thermoplastic) and Resilon. Specimens (10 mm diameter x 1 mm thick; n=7 per condition) were prepared and maintained at 37 degrees C for 48 h. Each specimen was weighed on a precision scale every 24 h until its mass was stable, at which time the i...
متن کاملRheological characterization of thermoplasticized injectable gutta percha and resilon
The effectiveness of a material to adequately seal the root canal space is related to its physical properties and handling characteristics. Since the introduction of the warm vertical compaction technique, the thermoplastic compaction of canal spaces has been broadly advocated. Warm gutta percha can be easily Rheological characterization of thermoplasticized injectable gutta percha and resilon
متن کاملThe Effect of Storage Temperature on Mechanical Properties of Gutta-Percha and Resilon
OBJECTIVES To compare the mechanical properties of Resilon and gutta-percha cones after storing at three different temperatures. MATERIALS AND METHODS One-hundred standardized size 40/02 gutta-percha cones and 100 Resilon cones were randomly divided into four groups. The first group of the materials were tested immediately after receipt as the control group. The other three were stored in the...
متن کاملInterfacial strength of Resilon and gutta-percha to intraradicular dentin.
Strengthening of Resilon-filled roots via an adhesive interface should be reflected by improvement in the interfacial strength and dislocation resistance between the root fillings and intraradicular dentin. This study compared the interfacial strengths of Resilon/Epiphany and gutta-percha/AH Plus using a thin-slice push-out test design. Failure modes of root slices after push-out testing were e...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
journal of dentistry, tehran university of medical sciencesجلد ۱۲، شماره ۲، صفحات ۱۳۴-۹
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023