Wear Properties of Gabbro Based Glass and Glass-Ceramic Materials
نویسندگان
چکیده
منابع مشابه
Wear Properties of Gabbro Based Glass and Glass-Ceramic Materials
Glass-ceramic materials were developed from gabbro including MgO and Al2O3 additives. Heat treatments for phase transformation from glassy matrix to glass-ceramic were carried out at 1000 ◦C for 3 h. X-ray di raction studies conducted on the glass-ceramic samples revealed that the phases formed in the glass-ceramics were cordierite, anorthite, diopsitic augite, forsterite and andesine. Glass an...
متن کاملGranite Based Glass-Ceramic Materials
In this study, production possibility of glass and glass-ceramic produced from granite was investigated. The composition of granite based glass bath mixture was 50 wt% granite, 25 wt% dolomite and 25 wt% sodium carbonate. Composition that was grounded and mixed in a ball mill for 2 h was melted at 1500 ◦C for 1 h. Glass samples were heat treated for crystallization to produce glass-ceramic mate...
متن کاملLuminescence Properties of Oxyfluoride Glass and Glass Ceramic Doped with Y3 + Ions
Oxyfluoride glass ceramics containing CaF2nano-crystals doped with Y3+ ions were prepared by one-step crystallization of SiO2- Al2O3- CaO- CaF2 glasses at different temperatures. X- ray diffraction (XRD) results have revealed that CaF2 was the only precipitated crystalline phase in glass ceramic samples. According to the XRD results, a glass ceramic was selected as the best sample in order to ...
متن کاملZirconia Toughening of Glass-ceramic Materials
A ceramic material suitable for packaging of large scale integrated circuit is produced by the process of forming a mixture of a powdered glass ceramic material which is a glassy precursor to cordierite ceramic material, formed by the steps which are as follows: a. Mix tetragonal phase material selected from the group consisting of zirconia or hafnia powder con taining a stabilizing oxide compo...
متن کاملProcessing Capability of Apatite-Mullite Glass-Ceramic Materials for the Production of Dental Restorations
Introduction: There is currently significant interest in all-ceramic dental restorations. A potential non-metallic material for such restorations is an apatite-mullite glass-ceramic that could be processed to shape using different processing techniques. The aim of this study was to assess and evaluate the ability of an apatite-mullite glass-ceramic material to be processed using three routes: l...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Physica Polonica A
سال: 2014
ISSN: 0587-4246,1898-794X
DOI: 10.12693/aphyspola.125.615