Wear Characteristic of the Zirconia-Alumina Grains

Crack growth resistance of alumina, zirconia and zirconia toughened alumina ceramics for joint prostheses.

Mono-phase bio-ceramics (alumina and zirconia) are widely used as femoral heads in total hip replacements (THR) as an alternative to metal devices. Unfortunately, the orthopaedic community reports significant in-vivo failures. Material scientists are already familiar with composites like alumina zirconia. Since both are biocompatible, this could prove to be a new approach to implants. This pape...

Detection of tetragonal zirconia in alumina–zirconia powders by thermoluminescence

The thermoluminescence (TL) after excitation by UV or X-rays radiation of alumina-zirconia powders is investigated. The composites present five of the characteristic peaks of zirconia at −170, −145, −90, 0 and 95 °C. After a thermal treatment of mixed oxides, a new peak is observed at −35 °C in TL. This peak reveals the presence of stabilized tetragonal zirconia in the material. Moreover by com...

Microseparation and stripe wear in alumina-on-alumina hip implants.

The combination of materials that still has highest wear resistance for total hip replacement is ceramic-on-ceramic. However, brittleness is a major concern for ceramics: in vivo and in vitro studies on ceramic hip prostheses correlate microseparation with hip noise, ceramic wear, or ceramic liner damage. Ceramic microseparation can lead to edge load, ceramic head wear, and squeaking. The aim o...

Elaboration of Alumina-Zirconia Composites: Role of the Zirconia Content on the Microstructure and Mechanical Properties

Alumina-zirconia (AZ) composites are attractive structural materials, which combine the high hardness and Young's modulus of the alumina matrix with additional toughening effects, due to the zirconia dispersion. In this study, AZ composites containing different amounts of zirconia (in the range 5-20 vol %) were prepared by a wet chemical method, consisting on the surface coating of alumina powd...

Fracture simulation for zirconia toughened alumina microstructure