Varistor performance of nanocrystalline Zn–Bi–O thin films prepared by reactive RF magnetron sputtering at room temperature
نویسندگان
چکیده
منابع مشابه
Varistor performance of nanocrystalline Zn–Bi–O thin films prepared by reactive RF magnetron sputtering at room temperature
The Zn–Bi–O films were deposited by reactive radio frequency magnetron sputtering in oxygen atmosphere from ZnBi alloy target (wt% ratio Zn:Bi=9:1) on glass substrate at room temperature. The XRD patterns show that the films deposited on tin-doped indium oxide/glass substrates were nanocrystalline. The microstructure of Bi-doped ZnO films was studied by scanning electron microscopy in combinati...
متن کاملColumnar Growth of Nanocrystalline ZnO Thin Films Prepared through RF Magnetron Sputtering
Nanocrystalline zinc oxide thinfilms have been prepared on glass substrates at different temperatures through planar RF-magnetron sputtering. The particle size reduction with respect to substrate temperature has been studied with x-ray 144 K. Saravanakumar et al diffraction (XRD) and atomic force microscopy (AFM). Cross-sectional transmission electron microscopic (TEM) studies employing dark-fi...
متن کاملNanocrystalline GaN and GaN:H Films Grown by RF-Magnetron Sputtering
The structural and optical properties of nanocrystalline GaN and GaN:H films grown by RF-magnetron sputtering are focused here. The films were grown using a Ga target and a variety of deposition parameters (N2/H2/Arflow rates, RF power, and substrate temperatures). Si (100) and fused silica substrates were used at relatively low temperatures (Ts ≤ 420K). The main effects resulting from the depo...
متن کاملCharacterization of PZT Ferroelectric Thin Films by RF-magnetron Sputtering
By using Radio Frequency (RF) magnetron sputtering method, Pb(Zr0.5Ti0.5)O3 (PZT) thin films were deposited on Pt/Ti/ SiO2/Si substrates. Pt/Ti bottom electrode was fabricated on SiO2/Si substrates by magnetron dual-facing-target sputtering system. Phase and crystalline structure analyses of the PZT films were performed on an X-ray diffraction(XRD), Surface morphology, roughness and particle si...
متن کاملThermoelectric and Transport Properties of Delafossite CuCrO2:Mg Thin Films Prepared by RF Magnetron Sputtering
P-type Mg doped CuCrO₂ thin films have been deposited on fused silica substrates by Radio-Frequency (RF) magnetron sputtering. The as-deposited CuCrO₂:Mg thin films have been annealed at different temperatures (from 450 to 650 °C) under primary vacuum to obtain the delafossite phase. The annealed samples exhibit 3R delafossite structure. Electrical conductivity σ and Seebeck coefficient S of al...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Vacuum
سال: 2004
ISSN: 0042-207X
DOI: 10.1016/j.vacuum.2003.12.141