Abstract—Sodium borosilicate glasses doped with different content of NdF3 mol % have been prepared by rapid quenching method. Ultrasonic velocities (both longitudinal and shear) measurements have been carried out at room temperature and at ultrasonic frequency of 4 MHz. Elastic moduli, Debye temperature, softening temperature and Poisson's ratio have been obtained as a function of NdF3 modifier...

PREPARATION OF Fe/GLASS COMPOSITE BY REDUCTION OF Na2O– Fe2O3–B2O3–SiO2–ZnO GLASS AND GLASS CERAMICS

In the present study, the feasibility of α-Fe ferromagnetic phase formation in glass and glass-ceramic by reduction in hydrogen atmosphere have been investigated. The glass with the composition of 35Na 2 O–24Fe2O3–20B 2O3 – 20SiO 2 –1ZnO (mol %) was melted and quenched by using a twin roller technique. As quenched glass flakes were heat treated in the range of 400-675 °C for 1-2 h in h...

CRYSTALLIZATION BEHAVIOUR OF GELS AND GEL-MONOLITHS IN THE Na2O-B2O3-SiO2 SYSTEM

BEHAVIOUR OF GERMANIUM IN PHASE SEPARABLE GLASSES OF THE SYSTEM Na2O - B2O3 - GeO2 - SiO2

The role of Ge02 in the Na20 B2O3 Ge02 Si02 quaternary system which presents a spinodal decomposition domain is studied. The physical properties of this system are compared to those of the system without Ge02. The leaching conditions of these glasses and the coordination of Ge are studied.

Bulk Crystallization in a SiO2/Al2O3/Y2O3/AlF3/B2O3/Na2O Glass: Fivefold Pseudo Symmetry due to Monoclinic Growth in a Glassy Matrix Containing Growth Barriers

A glass with the mol% composition 17 Y2O3·33 Al2O3·40 SiO2·2 AlF3·3 Na2O·2 CeF3·3 B2O3 is heat treated at 1000 °C for 6-24 h. This results in the surface nucleation and growth of YAG. Nucleation and growth of star-shaped alumina and later of monoclinic β-Y2Si2O7 and orthorhombic δ-Y2Si2O7 are additionally observed in the bulk. Phase identification and localization are performed by electron back...