Tungsten and Molybdenum Metallizings of High-Alumina Ceramics
نویسندگان
چکیده
منابع مشابه
Mullite-alumina functionally gradient ceramics
Cracks free mullite-alumina Functionally Gradient Ceramics (FGC) have been obtained by sequential slip casting of Mullite-alumina slurries with diserent mullite/alumina ratios. These slurries were prepared with 65 % solids content and viscosities rangingpom 10 to 40 mPa.s. 7he presence of cracks perpendicular to the FGC layers have been attributed to residual stresses developed because of the m...
متن کاملSurface Contamination of Alumina Ceramics by Carbon
Article history: Received: 01.05.2016. Received in revised form: 25.07.2016. Accepted: 06.09.2016. This study presents the results of investigating the cause of contamination of aluminum oxide ceramics (Al2O3) in the form of brown colored stain. Contaminated ceramic surfaces were examined with the scanning electron microscope (SEM) equipped with the Energy Dispersive Spectrometer (EDS). The res...
متن کاملComparison of doped combination zirconium-tungsten, zirconium- molybdenum and molybdenum-tungsten on single-wall vanadium oxide nanotube in hydrogen gas adsorption
In this study, doped vanadium oxide nanotubes were evaluated using different software to study the absorption of hydrogen gas. Vanadium oxide nanotubes are one of the options for absorption and storage hydrogen gas. In this research study for the first time, the Monte Carlo simulation was used to investigate the hydrogen gas absorption behavior in molybdenum-tungsten, molybdenum-zirconium and z...
متن کاملPyridine Adsorption on Molybdenum Oxide-Alumina Catalysts
The adsorption of pyridine on a complete monolayer molybdenum oxide-Al203 catalyst was studied. Both Lewis and Bronsted acid sites are present on a catalyst with a Mo valence of -4.1. The orientation of adsorbed pyridine was studied by means of its interaction with surface OD groups, which leads to the formation of only 2-deuteriopyridine. The fraction of molybdenum ions active for hydrogenatio...
متن کاملHertzian Contact Damage in Porous Alumina Ceramics
A study has been made of Hertzian contact damage in compressive shear stress field beneath the contact area. The observed microcrack density increases with grain size, porous and dense liquid-phase-sintered aluminas. Indentation stress–strain curves show increasing nonlinearity as the implying a threshold microstructural scale for crack initiation. In contrast, the micromechanisms controlling f...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 1990
ISSN: 0914-5400,1882-1022
DOI: 10.2109/jcersj.98.693