Three-dimensionally Ordered Macroporous Structure Enabled Nanothermite Membrane of Mn2O3/Al
Mn2O3 has been selected to realize nanothermite membrane for the first time in the literature. Mn2O3/Al nanothermite has been synthesized by magnetron sputtering a layer of Al film onto three-dimensionally ordered macroporous (3DOM) Mn2O3 skeleton. The energy release is significantly enhanced owing to the unusual 3DOM structure, which ensures Al and Mn2O3 to integrate compactly in nanoscale and...
متن کاملSpectral Radiative Properties of Three-dimensionally Ordered Macroporous Ceria Particles
Radiative properties of spherical heterogeneous particles consisting of threedimensionally ordered macroporous (3DOM) cerium dioxide (ceria) are numerically predicted in the spectral range 0.3–10μm. The particles are 1μm in diameter, with interconnected pores of diameter 330 nm and a face-centered cubic lattice arrangement. Predictions are obtained by solving macroscopic Maxwell’s equations usi...
متن کاملSynthesis of Three-Dimensionally Ordered Macroporous NiCe Catalysts for Oxidative Dehydrogenation of Propane to Propene
Three-dimensionally ordered macroporous (3DOM) NiCe catalysts with different Ni/Ce molar ratio were fabricated using the colloidal crystal templating method. The physic-chemical properties of the samples were characterized by various techniques, including N2 adsorption–desorption, X-ray diffraction (XRD), transmission electron microscopy (TEM), Raman, and H2-temperature-programmed reduction (TP...
متن کاملThree-dimensionally ordered macroporous carbons having walls composed of hollow mesosized spheres.
Three-dimensionally ordered macroporous carbons were prepared from bimodal polymer-silica colloidal crystals; the resulting carbons had interconnected macropores, and the walls of the macropores were composed of hollow mesosized spheres.
متن کاملThree-dimensionally ordered macroporous Cu2O/Ni inverse opal electrodes for electrochemical supercapacitors.
With an ordered polystyrene (PS) template-assisted electrochemical approach we synthesized three-dimensional ordered macroporous (3DOM) Cu2O/Ni inverse opals as electrodes for supercapacitors. The 3DOM Cu2O/Ni electrodes display superior kinetic performance, and satisfactory rate capability and cycling performance.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Scientific Reports
سال: 2016
ISSN: 2045-2322
DOI: 10.1038/srep22588