Thermographic Method Based Accelerated Fatigue Limit Calculation for Steel X5CrNi18-10 Subjected to Rotating Bending
نویسندگان
چکیده
منابع مشابه
Assessment of different methods for fatigue life prediction of steel in rotating bending and axial loading
Generally, fatigue failure in an element happens at the notch on a surface where the stress level rises because of the stress concentration effect. The present paper investigates the effect of a notch on the fatigue life of the HSLA100 (high strength low alloy) steel which is widely applicable in the marine industry. Tensile test was conducted on specimens and mechanical properties were obtain...
متن کاملassessment of different methods for fatigue life prediction of steel in rotating bending and axial loading
generally, fatigue failure in an element happens at the notch on a surface where the stress level rises because of the stress concentration effect. the present paper investigates the effect of a notch on the fatigue life of the hsla100 (high strength low alloy) steel which is widely applicable in the marine industry. tensile test was conducted on specimens and mechanical properties were obtain...
متن کاملBending Fatigue Failures in Valve Steel
In the present paper the effect of defects (viz. pits, gouges and oxide inclusions) will be reported. Although certain defects were uniformly distributed over the specimen surface, the majority of all fractures started in the edge region. An explanation to this behaviour is presented in terms of stress enhancement in the edge regions due to edge deflections.
متن کاملFatigue of Reinforcing Steel Bars Subjected to Natural Corrosion
Under badly environmental conditions as well as complex loads, corrosion of embedded reinforcing steel bars in concrete is common for reinforced concrete (RC) structures. Fatigue of corrosion reinforcing steel bars is a key problem for old RC bridges. To assess the residual fatigue life of aged existing RC bridges, the most new study information on fatigue of natural corrosion reinforcement is ...
متن کاملFatigue Properties of the Ultra-High Strength Steel TM210A
This paper presents the results of an experiment to investigate the high cycle fatigue properties of the ultra-high strength steel TM210A. A constant amplitude rotating bending fatigue experiment was performed at room temperature at stress ratio R = -1. In order to evaluate the notch effect, the fatigue experiment was carried out upon two sets of specimens, smooth and notched, respectively. In ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Polish Maritime Research
سال: 2015
ISSN: 2083-7429
DOI: 10.1515/pomr-2015-0073