The Oxide Scale Formation and Evolution on Detonation Gun Sprayed NiCrAlY Coatings during Isothermal Oxidation
نویسندگان
چکیده
منابع مشابه
A Review on Detonation Gun Sprayed Coatings
Materials are precious resources. Different methods are employed to protect the material from degradation. Thermal spraying is one of the most effective method to protect the material from wear, high temperature corrosion, stresses and erosion, thus increasing the life of material in use. Detonation gun spraying is one of the thermal spraying techniques known for providing hard, wear resistant ...
متن کاملsimulation and experimental studies for prediction mineral scale formation in oil field during mixing of injection and formation water
abstract: mineral scaling in oil and gas production equipment is one of the most important problem that occurs while water injection and it has been recognized to be a major operational problem. the incompatibility between injected and formation waters may result in inorganic scale precipitation in the equipment and reservoir and then reduction of oil production rate and water injection rate. ...
formation and evolution of regional organizations: the case study of the economic cooperation organization (eco)
abstract because of the many geopolitical, geo economical and geo strategically potentials and communicational capabilities of eco region, members can expand the convergence and the integration in base of this organization that have important impact on members development and expanding peace in international and regional level. based on quality analyzing of library findings and experts interv...
15 صفحه اولSuspension Plasma Sprayed Titanium Oxide and Hydroxyapatite Coatings
The paper aims at development of TiO2, Ca5(PO4)3OH (hydroxyapatite, HA) and their multilayer coatings onto stainless steel, titanium and aluminum substrate using suspension plasma spraying. The total thickness of the coatings was in the range 10 to 150 μm. The suspension on the base of distilled water, ethanol and their mixtures was formulated with the use of fine commercial TiO2 pigment crysta...
متن کاملIsothermal Oxidation of Aluminized Coatings on High-Entropy Alloys
The isothermal oxidation resistance of Al0.2Co1.5CrFeNi1.5Ti0.3 high-entropy alloy is analyzed and the microstructural evolution of the oxide layer is studied. The limited aluminum, about 3.6 at %, leads to the non-continuous alumina. The present alloy is insufficient for severe circumstances only due to chromium oxide that is 10 μm after 1173 K for 360 h. Thus, the aluminized high-entropy allo...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2007
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.mra2007091