Texture Evolution and Anisotropy of Plastic Flow in Hot Compression of Extruded ZK60-T5 Magnesium Alloy Plate
نویسندگان
چکیده
منابع مشابه
Investigation of Ca in the Microstructural Evolution and Porosity Analysis of ZK60 Alloy in As-Cast and Extruded Conditions
This research work has been carried out to study the effect of different Ca contents (0.5, 1.0, 1.5, 2.0 and 3.0) on the microstructure and porosity content of ZK60 alloys. The samples were examined by using optical and scanning electron microscopy (SEM) to evaluate the modification efficiency of the alloy with different Ca concentrations. The cast specimens were modified, homogenized and extru...
متن کاملHot Deformation Mechanisms in AZ31 Magnesium Alloy Extruded at Different Temperatures: Impact of Texture
The hot deformation characteristics of AZ31 magnesium alloy rod extruded at temperatures of 300 °C, 350 °C and 450 °C have been studied in compression. The extruded material had a fiber texture with > < 0 1 10 parallel to the extrusion axis. When extruded at 450 °C, the texture was less intense and the > < 0 1 10 direction moved away from the extrusion axis. The processing maps for the material...
متن کاملGrain Refinement and Enhancement of Mechanical Properties of Hot Extruded Rare-Earth Containing Magnesium Alloy
The effects of rare earth addition and hot extrusion process on the grain refinement of magnesium alloy were studied. The as-cast Mg-6Al-1Zn (AZ61) alloy had the average grain size of ~ 64 µm and its microstructure consisted of α-Mg and Mg17Al12 phase. By partial substitution of Al with Gd to reach Mg-4.8Gd-1.2Al-1Zn alloy, it was observed that the Mg17Al12 phase disappeared and two new interme...
متن کاملEvolution of texture in an ultrafine and nano grained magnesium alloy
The evolution of texture was discussed during the formation of ultra-fine and nano grains in a magnesium alloy severely deformed through accumulative back extrusion (ABE). The microstructure and texture obtained after applying multiple deformation passes at temperatures of 100 and 250°C were characterized. The results showed that after single ABE pass at 100°C an ultrafine/nano grained microstr...
متن کاملThe effect of twinning on texture evolution during ECAP processing of an AM30 magnesium alloy
An AM30 magnesium alloy was processed through ECAP method at 200 °C. Optical and transmission electron microscopy as well as electron back scattered diffraction (EBSD) technique were employed to characterize the deformed microstructure. A partially recrystallized microstructure including ultrafine/nano structures was obtained. The area fraction of 49% was measured for the recrystallized regions...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metals
سال: 2019
ISSN: 2075-4701
DOI: 10.3390/met9111170