Taguchi Yöntemi Kullanılarak Sürtünme Kaynağı ile Birleştirilen AISI 431 ve AISI 1020 Bağlantılarının Kaynak Parametrelerinin Optimizasyonu

Martensitic stainless steel AISI 431 and low carbon 1020 are materials used together in many different industries. However, important problems encountered when welding (fusion welding) these to each other. For this reason, friction process (Solid-state is join dissimilar metals. There very few studies on joining with welding. Therefore, the optimization of parameters pairs great important. In addition, effects factors dependent need be well understood. study, bars were successfully joined by welding, tensile strength axial shortening investigated, optimized using Taguchi method obtain quality weld joints. The experimental results study showed that highest (573.32 MPa) joints was 54.53%, higher than lowest (370.99 MPa), (23.18 mm) 650.16%, (3.09 mm). optimal for average determined as A3B1C3 A3B3C2; percentage contribution values found 51.55% (rotating speed) 63.90% speed); R2 strengths 97% 99.3%, respectively.