Synthesis of Hexaferrite Nanoparticles by Spray Pyrolysis Method
نویسندگان
چکیده
منابع مشابه
Synthesis of ZnO Nanoparticles by Spray Pyrolysis Method
Zinc oxide (ZnO) nanoparticles were synthesized by spray pyrolysis method using an aqueous solution of zinc acetate at various concentrations from 5 to 25 wt%. The decomposition of precursor solutions was carried out at 800, 1000 and 1200ºC under different atomizing pressures. The crystal structure and morphology of synthesized nanoparticles were characterized by X-Ray Diffraction ...
متن کاملsynthesis of zno nanoparticles by spray pyrolysis method
zinc oxide (zno) nanoparticles were synthesized by spray pyrolysis method using an aqueous solution of zinc acetate at various concentrations from 5 to 25 wt%. the decomposition of precursor solutions was carried out at 800, 1000 and 1200ºc under different atomizing pressures. the crystal structure and morphology of synthesized nanoparticles were characterized by x-ray diffraction (xrd) spectro...
متن کاملSurfactant-assisted synthesis of Barium hexaferrite nanoparticles by hydrothermal method
In the present work, the synthesis of Barium hexaferrite (BaFe12O19) nanoparticles in thepresence of a large excess amount of OH− anions by the hydrothermal method in the presence and absence of surfactants such as Sodium dodecyl benzene sulfonate and Triton X-114 was reported. The optimized temperature in the absence of surfactant was determined (200 °C) and then Barium hexaferrite nanoparticl...
متن کاملsurfactant-assisted synthesis of barium hexaferrite nanoparticles by hydrothermal method
in the present work, the synthesis of barium hexaferrite (bafe12o19) nanoparticles in thepresence of a large excess amount of oh− anions by the hydrothermal method in the presence and absence of surfactants such as sodium dodecyl benzene sulfonate and triton x-114 was reported. the optimized temperature in the absence of surfactant was determined (200 °c) and then barium hexaferrite nanoparticl...
متن کاملCubic or monoclinic Y2O3:Eu nanoparticles by flame spray pyrolysis
Monocrystalline cubic and/or monoclinic Y2O3:Eu nanoparticles (10-50 nm) were synthesized continuously without post-processing by single-step flame spray pyrolysis (FSP). These particles were characterized by Xray diffraction (XRD), nitrogen adsorption (BET) and transmission electron microscopy (TEM). Photoluminescence (PL) emission was measured as well as the time-resolved PL-intensity decay. ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 2004
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.51.795