Study on Microstructure of Pack-Borided GH4169 Alloy
نویسندگان
چکیده
Abstract The structure of the solid pack-boriding layer nickel-based alloy is studied in this paper. GH4169 was subjected to treatment at 850 °C and 950 °C, boriding studied. After treatment, a relatively continuous uniform formed on surface, which mainly composed nickel borides chromium borides. sample layered layer, diffusion zone, substrate. Cr migrated surface form CrB, 5 B 3 , 2 borides, while Ni lower part
منابع مشابه
a study on construction of iranian life tables: the case study of modified brass logit system
چکیده ندارد.
15 صفحه اولSURFACE HARDENING OF TUNGSTEN-BASED HEAVY ALLOY VIA PACK BORONIZING
The boronizing of a tungsten heavy alloy containing Ni and Fe as the major alloying elements were performed in the present study to increase its surface hardening. Pack cementation method was employed as a well-known, successful solid-state process for boronizing. The coating treatment was accomplished at different temperatures of 1000, 1050 and 1100°C for 6 and 9 hours. The formation of tu...
متن کاملstudy of hash functions based on chaotic maps
توابع درهم نقش بسیار مهم در سیستم های رمزنگاری و پروتکل های امنیتی دارند. در سیستم های رمزنگاری برای دستیابی به احراز درستی و اصالت داده دو روش مورد استفاده قرار می گیرند که عبارتند از توابع رمزنگاری کلیددار و توابع درهم ساز. توابع درهم ساز، توابعی هستند که هر متن با طول دلخواه را به دنباله ای با طول ثابت تبدیل می کنند. از جمله پرکاربردترین و معروف ترین توابع درهم می توان توابع درهم ساز md4, md...
ذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of physics
سال: 2023
ISSN: ['0022-3700', '1747-3721', '0368-3508', '1747-3713']
DOI: https://doi.org/10.1088/1742-6596/2578/1/012039