Solid-State Additive Deposition of AA7075 on AZ31B Substrate: Heat Treatment to Improve the Corrosion Fatigue Resistance
نویسندگان
چکیده
The influence of heat treatment on the coating microstructure, nanomechanical, and corrosion fatigue properties solid-state deposition AA7075 aluminum alloy AZ31B cast Mg is studied in detail. Transmission electron microscopy (TEM) microstructural analysis shows columnar grain at interface AA7075/AZ31B. Electron backscatter diffraction (EBSD) observation discovered elongated grains with a high fraction deformed boundaries as-deposited heat-treated 200 °C conditions. In contrast, annealed samples show recrystallized increasing temperatures from to 400 °C. residual stress surface subsurface measured by X-ray −55 MPa −122 MPa, respectively, which transferred tensile annealing temperature up Annealing considerably improved nanomechanical resistance. With °C, hardness decreased, while modulus increased significantly. fracture surfaces revealed that corrosive solution entered through cracks accelerated crack propagation, lowering life. However, presence
منابع مشابه
Investigation into heat treatment and residual stress in laser clad AA7075 powder on AA7075 substrate
The laser cladding of AA7075 powder onto a AA7075 substrate was conducted to evaluate the effect of heat treatment and measure residual stress between the clad layer and substrate in order to better understand the effect of laser cladding. The microstructure formed in the clad region was characteristic of a high cooling rate, which is typical for laser cladding. The heat affected zone showed co...
متن کاملLoad Controlled Fatigue of AZ31B
With the expanding demand on application of magnesium alloys in automotive and aerospace industries, robust methods in fatigue characterization of commercially available magnesium alloys with high specific strength is anticipated. In this paper, rotating bending load controlled tests has been studied on specimens machined from an extrusion piece of AZ31B. Due to asymmetric and anisotropic behav...
متن کاملElectrophoretic deposition and corrosion behavior study of aluminum coating on AZ91D substrate
Aluminum coating was prepared on AZ91D magnesium alloy substrate using the electrophoretic deposition (EPD) method in absolute ethanol solvent. In order to determine the optimal concentration of AlCl3.6H2O additive, the zeta potential and size of particles in the suspension were measured in the presence of different concentrations of AlCl3.6H2O. The results showed that an appropriate coating is...
متن کاملInfluence the heat treatment of two base metal alloys used on dental prosthesis on corrosion resistance
Purpose: The goal of the study is to try find the influence of the heat treatment on the corrosion resistance of two base cobalt alloys used on dental prosthesis. Design/methodology/approach: The investigation was choosen two base cobalt alloys: Remanium 2000+ (Dentaurum) and Wirobond LFC (Bego). Corrosion resistance test were carried out at room temperature and use of the Potentiostat IPS AJ P...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metals
سال: 2022
ISSN: ['2075-4701']
DOI: https://doi.org/10.3390/met12101578