Shock consolidation of Fe-based amorphous alloy powder.
نویسندگان
چکیده
منابع مشابه
KINETICS OF -Fe NANOCRYSTALLIZATION IN Fe55Cr18Mo7B16C4 BULK AMORPHOUS ALLOY
Abstract: In this research work, crystallization kinetics of Fe55Cr18Mo7B16C4 alloy was evaluated by X-ray diffraction, TEM observations and differential scanning calorimetric tests. In practice, crystallization and growth mechanisms were investigated using DSC tests in four different heating rates. Results showed that a two -step crystallization process occurred in the alloy in which - Fe phas...
متن کاملHydrogen Effects on an Amorphous Fe-Si-B Alloy
HYDROGEN interaction with amorphous alloys has Ribbons (,25-mm thick) of amorphous Fe80B11Si9 were been studied extensively due to both scientific and technoused for this research. The ribbons were produced by planarlogical interest. In the framework of a more comprehensive flow casting and were kindly supplied by AlliedSignal Inc. investigation of hydrogen interaction with amorphous and (Parsi...
متن کاملDEVELOPMENT OF HARDNESS IN A Fe- BASED NANO-COMPOSITE ALLOY
Achieving extreme hardness in the newly synthetic steel formed by converting from initial amorphous state to subse-quent crystalline structure –named as devitrification process- was studied in this research work. Results of TEM observa-tions and XRD tests showed that crystallized microstructure were made up four different nano-scale phases i.e., α-Fe, Fe 36 Cr12 Mo10 , Fe 3 C and Fe3 B. More, V...
متن کاملA DETAILED STUDY TOWARD THE NANO -CRYSTALLIZATION OF α – Fe IN Fe55-X Cr18Mo7B16C4 BULK AMORPHOUS ALLOY
Crystallization of α – Fe phase during annealing process of Fe55Cr18Mo7B16C4 bulk amorphous alloy has been evaluated by X- ray diffraction, differential scanning calorimetric tests and TEM observations in this research. In effect, crystallization mechanism and activation energy of crystallization were evaluated using DSC tests in four different heating rates (10, 20, 30, 40 K/min). A two -st...
متن کاملStructural Evolution during Milling, Annealing, and Rapid Consolidation of Nanocrystalline Fe–10Cr–3Al Powder
Structural changes during the deformation-induced synthesis of nanocrystalline Fe-10Cr-3Al alloy powder via high-energy ball milling followed by annealing and rapid consolidation by spark plasma sintering were investigated. Reduction in crystallite size was observed during the synthesis, which was associated with the lattice expansion and rise in dislocation density, reflecting the generation o...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 1988
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.35.742