Preparation of Cr-C alloy plating from Cr(III)sulfate-carboxylate baths.
نویسندگان
چکیده
منابع مشابه
Electrodeposition and Characterization of Sn-Zn Alloy Coatings from Sulfate Based Baths
Tin-Zinc alloy coatings have many applications because of their unique properties such as corrosion resistance, solderability and flexibility. In this study, the effect of current density, temperature and pH on chemical composition, cathodic current efficiency, morphology and structures of the coatings was investigated. The results illustrated that, at low current densities (<0.5 mA/cm2), the c...
متن کاملElectroless Nickel Plating on Magnesium Alloy
he inherent lightness and good strength-to-weight ratio of T magnesium has focused attention on increasing applications in aerospace and allied fields. Its density is two thirds that of aluminum-a conventional structure material for aerospace. Magnesium has one drawback: It is prone to atmospheric corrosion. Further, because of its high chemical affinity for aqueous solutions, it is categorized...
متن کاملZinc-Alloy-Plating for Corrosion Protection
Zinc represents the most effective and economic corrosion protection especially for steel base materials. Improved corrosion resistance can be achieved by alloying zinc with small amounts (around 1 Yo) of transition metal elements like Co, Ni and Fe. Zn-Fe and Zn-Co alloys containing up to 1.5 Yo of the transition metal were plated using an alkaline and acidic electrolyte respectively. Zn-Ni al...
متن کاملProlonging the Life of Electroless Nickel Plating Baths by Phosphite Removal
Electroless nickel plating baths have to be discarded when levels of phosphites build up and interfere with the plating process. OWMC funded research conducted at ORTECH International to determine whether phosphites could be removed from plating bath solution. The first attempt to do this by adsorption on flyash was unsuccessful. However, the use of calcium ion to precipitate calcium phosphite ...
متن کاملGrowth characteristics of primary M7C3 carbide in hypereutectic Fe-Cr-C alloy
The microstructure of the hypereutectic Fe-Cr-C alloy is observed by optical microscopy (OM). The initial growth morphology, the crystallographic structure, the semi-molten morphology and the stacking faults of the primary M7C3 carbide are observed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The in-suit growth process of the primary M7C3 carbide was observe...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Surface Finishing Society of Japan
سال: 1991
ISSN: 0915-1869,1884-3409
DOI: 10.4139/sfj.42.95