Oxidation of a chromia-forming nickel base alloy at high temperature in mixed diluted CO/H2O atmospheres
نویسندگان
چکیده
منابع مشابه
High Temperature Oxidation Behaviour of Nimonic - 115 Alloy in Presence of Sodium Salts at 850OC
The high temperature oxidation behaviour of Nimonic-115 industrial alloy has been investigated in presence of NaNO3, Na2CO3 and Na2O2 at 850oC in flowing air. The oxidation kinetics and effect of salt deposition for the period of 48 h were studied. The scale morphologies were determined on the basis of X-ray diffraction anal...
متن کاملNickel Base Superalloy Rene®80 – The Effect of High Temperature Cyclic Oxidation on Platinum-Aluminide Coating Features
Nickel base superalloy alloys are used in the manufacture of gas turbine engine components, which in use are exposed to high temperatures and corrosive environments. The platinum aluminide coatings described here have been developed to protect nickel base superalloy alloys from oxidation. In this study, the effect of cyclic oxidation, platinum layer thickness and aluminizing process on beha...
متن کاملhigh temperature oxidation behaviour of nimonic - 115 alloy in presence of sodium salts at 850oc
the high temperature oxidation behaviour of nimonic-115 industrial alloy has been investigated in presence of nano3, na2co3 and na2o2 at 850oc in flowing air. the oxidation kinetics and effect of salt deposition for the period of 48 h were studied. the scale morphologies were determined on the basis of x-ray diffraction analysis and scanning electron microscopic techniques. it has been shown t...
متن کاملHigh Temperature Erosion- Oxidation Behavior of Nickel- Based Alloys Containing Mo in Fluidized Bed Waste Incineration
High-temperature erosion-oxidation behavior of nickel-based alloys containing 0-7 wt.% Mo in fluidized bed waste incineration conditions was studied. A stream of hot condensed air with a flow rate of 25 L/min caused hot silica sand (700 °C) mixed with 0.5 wt.% of chloride salts to hit the specimens for 250 h. By removing the erosive factor, the high-temperature oxidation behavior of the alloys ...
متن کاملHigh frequency fatigue crack propagation behavior of a nickel-base turbine disk alloy
Fatigue crack propagation tests were conducted on the powder metallurgy nickel-base superalloy KM4 at room temperature. Two different heat treatments were investigated, one which produced a relatively coarse grain size around 55 μm, and another which produced a very fine grain size around 6 μm. Tests were conducted at 50 Hz and 1000 Hz in an advanced servohydraulic testing machine at R-ratios b...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Corrosion Science
سال: 2009
ISSN: 0010-938X
DOI: 10.1016/j.corsci.2009.01.019