A Practical Engineering Approach to Predicting Fatigue Crack Growth in Riveted Lap Joints
An extensive experimental database has been assembled from very detailed teardown examinations of fatigue cracks found in rivet holes of fuselage structural components. Based on this experimental database, a comprehensive analysis methodology was developed to predict the onset of widespread fatigue damage in lap joints of fuselage structure. Several computer codes were developed with specialize...
متن کاملOn the Influence of Riveting Process Parameters on Fatigue Life of Riveted Lap Joint
In this paper, influence of riveting process parameters, namely, riveting force, sheet thickness, friction coefficient and clearance fit are investigated on residual stress field and fatigue life of single riveted lap joint of AA2024 type. According to the effect of riveting induced residual stresses on fatigue life of riveted lap joint, these parameters are optimized to maximize the residual s...
متن کاملFatigue Crack Growth in Adhesive Joints
Adhesive joining is recognized as a potential enabling technology for a variety of material systems being considered in automotive structures where traditional fastening methods would be inappropriate. Well known examples include fiber reinforced composites and polymers. Additionally in certain circumstances, adhesive bonding of steel structures can provide benefits such as improved stiffness a...
متن کاملFatigue behaviour of composite adhesive lap joints
This paper is concerned with a fatigue study of composite adhesive lap joints produced from a bi-directional woven E-glass fibres and polypropylene. The adhesive used was a Bostik 7452 (Rubber & Plastics Grade) ethyl cyanoacrylate type. The effects of layer orientation, lap joint length and water immersion on the fatigue behaviour were studied. The specimens were immersed in water during period...
متن کاملFatigue Life Prediction for Welded Joints with Known Initial Crack
The inspection of various structures often detects a fatigue cracks developed during long service life. These fatigue cracks significantly reduce remaining fatigue life and fatigue strength. Influence of the initial fatigue cracks size in non-load-carrying fillet-welded one-sided transverse attachment joints on the remaining fatigue life and fatigue strength is considered in this paper. A compu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Mechanics and Control
سال: 2012
ISSN: 2083-6759
DOI: 10.7494/mech.2012.31.3.108