Nano-Wollastonite in Particleboard: Physical and Mechanical Properties
The effects of wollastonite nanofibers on the physical and mechanical properties of particleboard were studied. Nano-wollastonite (NW), with the size range of 30 to 110 nm, was applied at 5, 10, 15, and 20%, based on the dry weight of wood chips, and compared with control specimens. Two application methods of NW were used: surface application (SA) and internal application (IA). Density was kept...
متن کاملdetermination of some physical and mechanical properties red bean
چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...
15 صفحه اولEffects of Nano-wollastonite on Physical and Mechanical Properties of Medium-density Fiberboard
Effects of nano-wollastonite (NW) on physical and mechanical properties of medium density fiberboard (MDF) were studied. NW was applied at 5, 10, 15, and 20 g/kg dry weight basis of wood fibers; the results were then compared with control specimens. Two application methods of NW were used: surface and internal applications. Density was kept constant at 0,67 g/cm3 for all treatments and tests we...
متن کاملPhysical and Mechanical Properties of Particleboard from Bamboo Waste
This research was to evaluate a technical feasibility of making single-layer experimental particleboard panels from bamboo waste (Dendrocalamus asper Backer) by converting bamboo into strips, which are used to make laminated bamboo furniture. Variable factors were density (600, 700 and 800 kg/m) and temperature of condition (25, 40 and 55 C). The experimental panels were tested for their physic...
متن کاملEVALUATION OF THE MECHANICAL AND PHYSICAL PROPERTIES OF PARTICLEBOARD MANUFACTURED FROM CANOLA (Brassica napus) STRAWS
This study examined possible feasibility of canola (Brassica napus) straws in the production of particleboard. Three-layer experimental particleboards with density 0,7 g/cm3 were manufactured using different canola straws particle ratios (0%, 25%, 50%, 75% and 100%) and urea formaldehyde (UF) adhesive. Modulus of elasticity (MOE), modulus of rupture (MOR), internal bond strength (IB), water abs...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: BioResources
سال: 2013
ISSN: 1930-2126
DOI: 10.15376/biores.8.4.5721-5732