N-doped carbon modified Pt/CNTs synthesized by atomic layer deposition with enhanced activity and stability for methanol electrooxidation
نویسندگان
چکیده
منابع مشابه
3D-nanoarchitectured Pd/Ni catalysts prepared by atomic layer deposition for the electrooxidation of formic acid
Three-dimensionally (3D) nanoarchitectured palladium/nickel (Pd/Ni) catalysts, which were prepared by atomic layer deposition (ALD) on high-aspect-ratio nanoporous alumina templates are investigated with regard to the electrooxidation of formic acid in an acidic medium (0.5 M H2SO4). Both deposition processes, Ni and Pd, with various mass content ratios have been continuously monitored by using...
متن کاملIntroduction to (plasma-enhanced) atomic layer deposition
Film growth by the atomic layer deposition (ALD) method relies on alternate pulsing of the precursor gases and vapors into a vacuum chamber and their subsequent chemisorption on the substrate surface (Fig. 1) [1,2]. The different steps in the process are saturative such that ALD film growth is self-limiting yielding one submonolayer of film per deposition cycle. ALD has some unique characterist...
متن کاملBiomimetic layer-by-layer deposition assisted synthesis of Cu, N co-doped TiO2 nanosheets with enhanced visible light photocatalytic performance.
In this paper, a Cu, N co-doped TiO2 nanosheet with increased visible light photocatalytic activity was successfully synthesized using a biomimetic layer-by-layer deposition process. The polymer, branched-polyethyleneimine (b-PEI) was used as an induction agent for the hydrolysis of titanium bis(ammonium lactato)-dihydroxide (Ti-BALDH) as well as for a nitrogen resource, and the graphene oxide ...
متن کاملAtomic layer deposition of Al2O3 on V2O5 xerogel film for enhanced lithium-ion intercalation stability
V2O5 xerogel films were fabricated by casting V2O5 sols onto fluorine-doped tin oxide glass substrates at room temperature. Five, ten and twenty atomic layers of Al2O3 were grown onto as-fabricated films respectively. The bare film and Al2O3-deposited films all exhibited hydrous V2O5 phase only. Electrochemical impedance spectroscopy study revealed increased surface charge-transfer resistance o...
متن کاملThe Enhanced Catalytic Performance and Stability of Rh/γ-Al2O3 Catalyst Synthesized by Atomic Layer Deposition (ALD) for Methane Dry Reforming
Rh/γ-Al₂O₃ catalysts were synthesized by both incipient wetness impregnation (IWI) and atomic layer deposition (ALD). The TEM images of the two catalysts showed that the catalyst from ALD had smaller particle size, and narrower size distribution. The surface chemical states of both catalysts were investigated by both XPS and X-ray Absorption Near Edge Structure (XANES), and the catalyst from IW...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Chinese Journal of Catalysis
سال: 2018
ISSN: 1872-2067
DOI: 10.1016/s1872-2067(18)63066-9