Micro-Crack Propagation and Fatigue Life of Large Welded Structures.
نویسندگان
چکیده
منابع مشابه
Fatigue Crack Detection and Sizing in Welded Steel Structures
The paper gives an outline of the non-destructive evaluation (NDE) methods currently being pursued at the Admiralty Marine Technology Establishment, Dunfermline, Scotland. The methods are being used to locate and characterise fatigue cracks in high yield strength welded steel structures. The techniques have been applied principally to large fatigue models (5' and 9' diameter) as part of a compr...
متن کاملFatigue Life Assessment of Welded Joints Considering Crack Propagation Based on Hot Spot Stress
In this study, fatigue test and crack propagation analysis of welded joints in ships and offshore structures were performed. The test models have two types of welded joints, T-joint and double plate. Test data is presented in S-N curves obtained by the Hot Spot Stress (HSS) approach. The S-N data for each length of crack were appraised to define the fatigue life of crack initiation and propagat...
متن کاملFatigue Life Prediction for Welded Joints with Known Initial Crack
The inspection of various structures often detects a fatigue cracks developed during long service life. These fatigue cracks significantly reduce remaining fatigue life and fatigue strength. Influence of the initial fatigue cracks size in non-load-carrying fillet-welded one-sided transverse attachment joints on the remaining fatigue life and fatigue strength is considered in this paper. A compu...
متن کاملProbabilistic model for fatigue crack growth and fracture of welded joints in civil engineering structures
This paper presents a probabilistic assessment model for linear elastic fracture mechanics (LEFM). The model allows the determination of the failure probability of a structure subjected to fatigue loading. The distributions of the random variables for civil engineering structures are provided, and the relative importance of these random variables is determined. An example of a bridge detail is ...
متن کاملFatigue Life of Repaired Welded Tubular Joints
In this study, the effect of repair on fatigue life of tubular joints is investigated. Six cracked specimens precedently subjected to fatigue loading undergone to weld repair. Two of those specimens were shot peened before primary fatigue loading. It is shown that repair gives rise to about 150% increase in fatigue life for original specimens while the increase of fatigue life for shot-peened ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1995
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.44.65