Matrix cracking of fiber-reinforced ceramic composites in shear
نویسندگان
چکیده
منابع مشابه
Matrix cracking of fiber-reinforced ceramic composites in shear
The mechanics of cracking in fiber-reinforced ceramic matrix composites (CMCs) under general loadings remains incomplete. The present paper addresses one outstanding aspect of this problem: the development of matrix cracks in unidirectional plies under shear loading. To this end, we develop a model based on potential energy differences upstream and downstream of a fully bridged steady-state mat...
متن کاملThermal resistance of bridged cracks in fiber-reinforced ceramic composites
The thermal resistance of a bridged matrix crack in a fiber-reinforced ceramic composite is analyzed. The problem is cast in terms of a unit cell comprising an infinitely long composite cylinder with a single matrix crack perpendicular to the fiber axis. At the outset, it is demonstrated that the thermal resistance of such a crack can be represented by a simple circuit consisting of two paralle...
متن کاملComputational modeling of damage evolution in unidirectional fiber reinforced ceramic matrix composites
A ®nite element model for investigating damage evolution in brittle matrix composites was developed. This modeling is based on an axisymmetric unit cell composed of a ®ber and its surrounding matrix. The unit cell was discretized into linearly elastic elements for the ®ber and the matrix and cohesive elements which allow cracking in the matrix, ®ber-matrix interface, and ®ber. The cohesive elem...
متن کاملAnomaly Detection and Microstructure Characterization in Fiber Reinforced Ceramic Matrix Composites
ANOMALY DETECTION AND MICROSTRUCTURE CHARACTERIZATION IN FIBER REINFORCED CERAMIC MATRIX COMPOSITES Name: Bricker, Stephen E. University of Dayton Advisor: Dr. Russell Hardie Ceramic matrix composites (CMCs) have the potential to replace current superalloys being used in hot components of jet engines. CMCs with continuous fiber reinforcement exhibit significant strength retention beyond tempera...
متن کاملWear of ceramic particle-reinforced metal-matrix composites
Wear experiments have shown that when the applied normal stress exceeds a critical value, a transition occurs from the regime of mild wear to that of adhesive wear. As a result, the wear rate of particle-reinforced aluminium composites increases by a hundred-fold. Based on dislocation and delamination theories, a criterion is proposed for determining the critical transition load, and a quantita...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Mechanics and Physics of Solids
سال: 2014
ISSN: 0022-5096
DOI: 10.1016/j.jmps.2014.08.007