Martensite-to-Austenite Reversion and Recrystallization in Cryogenically-Rolled Type 321 Metastable Austenitic Steel
نویسندگان
چکیده
منابع مشابه
Martensite ? austenite phase transformation kinetics in an ultrafine-grained metastable austenitic stainless steel
A generalized phase transformation kinetics model is used to understand the martensite to austenite transformation in a cold-rolled and annealed metastable AISI 301LN ultrafine-grained austenitic stainless steel. The model shows that the presence of interstitial nitrogen and heavy cold-rolling is important to promote fast transformation kinetics, through rapid nitrogen-diffusion and austenite n...
متن کاملKinetics of Austenite Recrystallization during the Annealing of Cold-rolled Fe-Mn-Al-C Steel
In the current study, the recrystallization behavior of 75% cold-rolled Fe-22Mn-10Al-1.4C steel during annealing at 750, 770, 790, 810, and 830°C was studied. X-ray diffraction patterns and optical microscopy were used to characterize microstructures. The Vickers Micro-hardness test was used to characterize recrystallization kinetics during annealing. Johnson-Mehl-Avrami-Kolmogorov (JMAK) model...
متن کاملInfluence of Annealing Treatment on the Formation of Nano/Submicron Grain Size AISI 301 Austenitic Stainless Steels
Nano/submicron austenitic stainless steels have attracted increasing attention over the past few years due to fine structural control for tailoring engineering properties. At the nano/submicron grain scales, grain boundary strengthening can be significant, while ductility remains attractive. To achieve a nano/ submicron grain size, metastable austenitic stainless steels are heavily cold-worked,...
متن کاملEffects of Martensite Reversion Parameters on the Formation of Nano/ultrafine Grain Structure in AISI 304L Stainless Steel
Formation of nano/ultrafine grain structure in AISI 304L austenitic stainless steel through the martensite reversion treatment was studied. The solution annealed specimens were cold rolled up to 95 % thickness reduction at -15°C. The cold-rolled specimens were subjected to reversion annealing treatment at the temperature range of 700-1000 °C for 10–150 min. Microstructural evolutions were analy...
متن کاملMicrostructural Evolution and Mechanical Properties of Ultrafine/nano Structured AISI 321 Stainless Steel Produced by Thermo-mechanical Processing
The mechanical properties and microstructural developments of 321 stainless steel during thermomechanical process were investigated. The repetitive cold rolling and subsequent annealing were conducted to achieve nanocrystalline structure in an AISI 321 stainless steel. Heavily cold rolling at −20°C was conducted to form martensite in metastable austenitic steel. The process was followed by anne...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metallurgical and Materials Transactions A
سال: 2018
ISSN: 1073-5623,1543-1940
DOI: 10.1007/s11661-018-5070-9