Isothermal Age-hardening Behaviour in a Multi-purpose Dental Casting Gold Alloy.
نویسندگان
چکیده
منابع مشابه
Isothermal age-hardening behaviour in commercial dental gold alloys containing palladium.
The isothermal age-hardening behaviour in the commercial dental gold alloys containing palladium was studied by means of resistometric, hardness, X-ray and electron microscopy. Drastic overageing occurred following prolonged ageing. The mechanism of the overageing was interpreted as a loss of coherency at the interfaces of the adjacent lamellae which consists of the equilibrium AuCu I ordered p...
متن کاملPrecipitation hardening in a dental low-gold alloy.
Age-hardening characteristics in a dental low-gold alloy composed of 40.0 wt% Au-35.0 wt% Ag-7.9 wt% Pd-7.0 wt% Cu-5.0 wt% In-3.5 wt% Zn-1.5 wt% Sn, were investigated by means of the hardness test, XRD study, SEM observations and EPMA. The following results were obtained. The age-hardening was characterized by a precipitation of Cu-rich alpha2 phase in the a phase. The softening that occurred f...
متن کاملDental casting of superelastic Ni-Ti alloy.
Rods of Ni-43.5wt% Ti alloy were prepared under various casting conditions. Specimens which were melted in a cordierite crucible and cast in a phosphate-bonded investment mold had less strength and elongation than those melted in a copper crucible and cast in a phosphate-bonded investment mold. All castings exhibited superelasticity at room temperature. The upper limit of recoverable strain was...
متن کاملSpinodal decomposition related to age-hardening and cuboidal structures in a dental low-carat gold alloy with relatively high Cu/Ag content ratio
A dental Au–Ag–Cu–Pd alloy with a relatively low Au content and a high Cu/Ag content ratio was examined to determine the correlation between the microstructural changes by the spinodal decomposition and age-hardening behaviour using a hardness test, X-ray diffraction study, field emission scanning electron microscopy and energy-dispersive X-ray spectrometry. Separation of the parent α0 phase oc...
متن کاملBase-metal dental casting alloy biocompatibility assessment using a human-derived three-dimensional oral mucosal model.
Nickel-chromium (Ni-Cr) alloys used in fixed prosthodontics have been associated with type IV Ni-induced hypersensitivity. We hypothesised that the full-thickness human-derived oral mucosa model employed for biocompatibility testing of base-metal dental alloys would provide insights into the mechanisms of Ni-induced toxicity. Primary oral keratinocytes and gingival fibroblasts were seeded onto ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Dental Materials Journal
سال: 1999
ISSN: 1881-1361,0287-4547
DOI: 10.4012/dmj.18.314