Irwin number and ductile-brittle fracture transition
نویسندگان
چکیده
منابع مشابه
Effect of Constraint on Ductile Crack Growth and Ductile-Brittle Fracture Transition of a carbon Steel
Ductile-brittle fracture transition was investigated using compact tension (CT) specimens from -70 o C to 40 o C for a carbon steel. Large deformation finite element analysis has been carried out to simulate the stable crack growth in the compact tension (CT, a/W=0.6), three point-point bend (SE(B), a/W=0.1) and centre-cracked tension (M(T), a/W=0.5) specimens. Experimental crack tip opening di...
متن کاملEngineering ductile fracture in brittle-matrix composites
This letter describes a newly discovered phenomenon: ductile fracture in cementitious materials. The brittle nature of materials such as concrete and ceramics has prompted the development of various approaches to enhance their fracture toughness. Fibre reinforcement has been the common focus in the toughening of the brittle materials. Two types of fracture have been observed to date in cementit...
متن کاملNumerical Modeling of the Ductile-Brittle Transition
Numerical studies of the ductile-brittle transition are described that are based on incorporating physically based models of the competing fracture mechanisms into the material's constitutive relation. An elastic-viscoplastic constitutive relation for a porous plastic solid is used to model ductile fracture by the nucleation and subsequent growth of voids to coalescence. Cleavage is modeled in ...
متن کاملExperimental and Numerical Investigation on Ductile-brittle Fracture Transition in a Magnesium Alloy
Tensile test on smooth and circumferentially notched specimens, systematic observation of fracture surfaces and large deformation finite element analysis were conducted to understand the deformation and failure behavior of a magnesium alloy (AM60). The plastic deformation is considered to be dominated by twining mediated slip. The tensile properties were not sensitive to the strain rates applie...
متن کاملFrom brittle to ductile fracture in disordered materials.
We introduce a lattice model able to describe damage and yielding in heterogeneous materials ranging from brittle to ductile ones. Ductile fracture surfaces, obtained when the system breaks once the strain is completely localized, are shown to correspond to minimum energy surfaces. The similarity of the resulting fracture paths to the limits of brittle fracture or minimum energy surfaces is qua...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Fracture
سال: 1996
ISSN: 0376-9429,1573-2673
DOI: 10.1007/bf00018531