Intermetallic Particle Evolution during ECAP Processing of a 6082 Alloy
نویسندگان
چکیده
منابع مشابه
The effect of twinning on texture evolution during ECAP processing of an AM30 magnesium alloy
An AM30 magnesium alloy was processed through ECAP method at 200 °C. Optical and transmission electron microscopy as well as electron back scattered diffraction (EBSD) technique were employed to characterize the deformed microstructure. A partially recrystallized microstructure including ultrafine/nano structures was obtained. The area fraction of 49% was measured for the recrystallized regions...
متن کاملAging Behaviour and Mechanical Properties of a Solution Treated and ECAP Processed 6082 Alloy
A study was carried out on the aging behaviour of a solution treated 6082 aluminium alloy deformed by equal channel angular pressing up to six passes. Aging of the so obtained ultrafine alloy was studied by DSC and TEM analyses as well as by isothermal treatments at 130, 160 and 180 C. The results showed that the formation of metastable 00 and 0 precipitates were markedly anticipated and that t...
متن کاملRecrystallization texture during ECAP processing of ultrafine/nano grained magnesium alloy
An ultrafine/nano grained AZ31 magnesium alloy was produced through four-pass ECAP processing. TEM microscopy indicated that recrystallized regions included nano grains of 75 nm. Pole figures showed that a fiber basal texture with two-pole peaks was developed after four passes, where a basal pole peak lies parallel to the extrusion direction (ED) and the other ~20° away from the transverse dire...
متن کاملAlNb intermetallic alloy
This investigation was conducted to ascertain the benefits of electropolishing after mechanical polishing for electron backscattered diffraction of a Ti 2 AlNb intermetallic Ti − 21Al − 29Nb (at.%) alloy containing the orthorhombic (O) and body-centered-cubic (BCC) phases. Electropolishing was performed at − 40 ° C in 6% H 2 SO 4 methanol solution. Atomic force microscopy was used to measure th...
متن کاملInfluence of Processing Techniques on Microstructure and Mechanical Properties of a Biodegradable Mg-3Zn-2Ca Alloy
New Mg-3Zn-2Ca magnesium alloy was prepared using different processing techniques: gravity casting as well as squeeze casting in liquid and semisolid states. Materials were further thermally treated; thermal treatment of the gravity cast alloy was additionally combined with the equal channel angular pressing (ECAP). Alloy processed by the squeeze casting in liquid as well as in semisolid state ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2004
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.45.2182