Influence of Microstructural morphology on Pitting Corrosion Resistance of Duplex Stainless Steel Weld Metals
نویسندگان
چکیده
منابع مشابه
Influence of multiple welding cycles on microstructure and corrosion resistance of a super duplex stainless steel
.......................................................................................... v Appended Publications .................................................................. vii Table of
متن کاملCorrosion Resistance and Semiconducting Properties of the Passive Films on Duplex Stainless Steel 2205
In this study, the effect of molybdate on the electrochemical behavior and semi-conductive properties of duplex stainless steel 2205 passive film at NaCl solutions was investigated. Cyclic potentiodynamic polarization, impedance spectroscopy, mott-schottky plots and scanning electron microscopy (SEM) were used to study the passive behavior. Polarization curves showed that the corrosion current ...
متن کاملInvestigation of Corrosion Behavior and Galvanic Corrosion Simulation of Super Duplex Stainless Steel UNS S32750 Weld Zone
Galvanic corrosion is an ever-present problem in all different environments, particularly in tanks. The goal of this project is to develop a finite element model that can be used with experimental data to characterize the corrosion of a galvanic weldments couple in an electrolyte. In this study sample are welded by gas tungsten arc welding and friction stir welding. According to ASTM G8, Evalua...
متن کاملMicrostructure, Pitting Corrosion Resistance and Impact Toughness of Duplex Stainless Steel Underwater Dry Hyperbaric Flux-Cored Arc Welds
Duplex stainless steel multi-pass welds were made at 0.15 MPa, 0.45 MPa, and 0.75 MPa pressure, simulating underwater dry hyperbaric welding by the flux-cored arc welding (FCAW) method, with welds of normal pressure as a benchmark. The purpose of this work was to estimate the effect of ambient pressure on the microstructure, pitting corrosion resistance and impact toughness of the weld metal. T...
متن کاملCrystallography of Widmanstätten austenite in duplex stainless steel weld metal
Two kinds of austenite grow from d-ferrite during the cooling of the duplex stainless steel weld deposits studied here, Widmanstätten plates and allotriomorphs which precipitate at d–d grain boundaries. It is found using microtexture measurements that the preferred crystallographic orientation of the Widmanstätten austenite can be estimated using established theory if it is assumed that there i...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY
سال: 2020
ISSN: 0288-4771,2434-8252
DOI: 10.2207/qjjws.38.263