Influence of Cr3C2 and VC Content on WC Grain Size, WC Shape and Mechanical Properties of WC–6.0 wt. % Co Cemented Carbides
نویسندگان
چکیده
منابع مشابه
FRACTURE AND FATIGUE BEHAVIOR OF WC-Co AND WC-CoNi CEMENTED CARBIDES
The fracture and fatigue characteristics of several cemented carbide grades are investigated as a function of their microstructure. In doing so, the influence of binder chemical nature and content (Co and 76wt%Co-24wt%Ni), as well as carbide grain size on hardness, flexural strength, fracture toughness and fatigue crack growth (FCG) behavior is evaluated. Mechanical testing is combined with a d...
متن کاملThe Effect of sintering temperature on microstructure and hardness of milled WC- 20 wt.% equiatomic (Fe,Co) cemented carbides
In this study, WC–20 wt.% equiatomic (Fe,Co) powder mixture was milled in a planetary ball mill. The effects of different milling time (15 min, 5h, 10h, and 25 h) and sintering temperatures on the microstructure and mechanical properties of this equi-Fe substituted cermet were investigated. The structural evolution and the crystallite size changes of the powders during milling were monitored by...
متن کاملFocused Ion Beam tomography of WC-Co cemented carbides
The microstructure of three different grades of WC-Co cemented carbides has been reconstructed in three dimensions after sequential images obtained by focused ion beam. The three-dimensional microstructual parameters are compared against the well-know two-dimensional parameters of grain size, phase percentages and mean free path. Results show good agreement with the exception of individual grai...
متن کاملGrinding effects on surface integrity and mechanical strength of WC-Co cemented carbides
In this study, the correlation existing among grinding, surface integrity, and flexural strength is investigated for WC-Co cemented carbides (hardmetals). A fine-grained WC-13 wt % Co grade and three different surface conditions: (1) ground, (2) mirror-like polished (reference), and (3) ground plus high-temperature annealed, are investigated. Surface integrity and mechanical characterization is...
متن کاملStudy of milling effect on particle size and mechanical properties of WC-Co composite
The effect of milling on the particle size and mechanical properties Tungsten Carbide - Cobalt composite were investigated. First, raw materials ratios by mechanical milling for 4 hours at 300 rpm were mixed. The powder in the optimum temperature 1350°C at a rate of temperature rise 50°C / min and shelf life of 4 minutes and the pressure MPa 30 were sintered in SPS. The results indicated nearly...