Increasing Mechanical Properties of 2-D-Structured Electrospun Nylon 6 Non-Woven Fiber Mats
نویسندگان
چکیده
منابع مشابه
Increasing Mechanical Properties of 2-D-Structured Electrospun Nylon 6 Non-Woven Fiber Mats
Tensile strength, Young's modulus, and toughness of electrospun nylon 6 non-woven fiber mats were improved by increasing individual nanofiber strength and fiber-fiber load sharing. Single-walled carbon nanotubes (CNTs) were used as reinforcement to increase the strength of the electrospun nylon 6 nanofibers. Young's modulus, tensile strength, and toughness of the nylon 6 non-woven fiber mats el...
متن کاملMechanical and tribological properties of electrospun PA 6(3)T fiber mats
The mechanical and tribological properties of electrospun fiber mats are of paramount importance to their utility as components in a large number of applications. Although some mechanical properties of these mats have been reported previously, reports of their tribological properties are essentially nonexistent. In this work, electrospun nanofiber mats of poly(trimethyl hexamethylene terephthal...
متن کاملCompressibility of electrospun fiber mats
Compressive properties of electrospun fiber mats are reported for the first time. Mats of bisphenol-A polysulfone (PSU) and of poly(trimethyl hexamethylene terephthalamide) (PA 6(3)T) were electrospun and annealed at a range of temperatures spanning the glass transition temperature of each polymer. The data for applied stress versus mat solidity were found to be well-described by a power law of...
متن کاملPhysical-chemical properties of cross-linked chitosan electrospun fiber mats
Chitosan fiber mats were successfully processed by electrospinning. The as-spun fiber mats were neutralized with ethanol and cross-linked with glutaraldehyde. A decrease of the fiber average diameter from 243 ± 43 nm down to 215.53 nm was observed for the neutralized and cross-linking chitosan membrane. It was found that the processing conditions do not alter the initial deacetylation degree of...
متن کاملStructural, mechanical, and tribological properties of electrospun poly(hexamethylene adipamide) fiber mats
The mechanical and tribological properties of electrospun fiber mats are of paramount importance to their utility in a large number of applications. In this work, mats of electrospun fibers of poly(hexamethylene adipamide) (PA 6,6) with average fiber diameter of 238 ± 22 nm are characterized for their crystal structure as well as their mechanical and tribological properties. Post-spin thermal a...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials
سال: 2016
ISSN: 1996-1944
DOI: 10.3390/ma9040270