Hot isostatic compaction of tool steel powders by visco-plastic pressure medium.
نویسندگان
چکیده
منابع مشابه
EVALUATING HOT DEFORMATION BEHAVIOR OF W360 TOOL STEEL BY HOT COMPRESSION TEST
In this research, the hot deformation behavior of W360 tool steel was investigated using hot compression test at 1000-1200°C and strain rates of 0.001, 0.01, 0.1, and 1 s-1. According to the results, dynamic recrystallization was found the most important restoration factor of this alloy during hot deformation. Recrystallization was enhanced with an increase in temperature and strain rate. Also,...
متن کاملHot Forming of Aisi A2 Tool Steel
In order to optimize the hot forming process of tool steels, further improvement of flow stress prediction and additional knowledge on hot deformability, especially at lower and upper limits of the hot working range, are required. The hot working ranges for these steels are very narrow as a consequence of the role of alloying elements, which form carbides. Carbides improve tool steel’s hardenab...
متن کاملEffects of Hot Isostatic Pressure on Titanium Nitride Films Deposited by Physical Vapor Deposition
Films of titanium nitride deposited by physical vapor deposition on 304 L stainless steel substrates were hot isostatic pressed (HIP) under 150 MPa at 550 °C. To study the effects of this treatment on the microstructure of those films, X-ray diffraction analyses, Rutherford Backscattering spectroscopy, scanning electron microscopy, and atomic force microscopy were performed. Surface hardness, a...
متن کاملSpark Plasma Co-Sintering of Mechanically Milled Tool Steel and High Speed Steel Powders
Hot work tool steel (AISI H13) and high speed steel (AISI M3:2) powders were successfully co-sintered to produce hybrid tool steels that have properties and microstructures that can be modulated for specific applications. To promote co-sintering, which is made difficult by the various densification kinetics of the two steels, the particle sizes and structures were refined by mechanical milling ...
متن کاملSimulation of Deformation and Hot Tear Formation Using a Visco-plastic Model with Damage
A three-phase model is presented that predicts solid deformation and damage as well as melt pressure, feeding flow and shrinkage porosity during metal casting. A visco-plastic constitutive theory with damage is used to model the solid deformation. Damage created by mechanically induced voiding is used as a hot tear indicator. The absence of liquid feeding determines when damage starts to form. ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 1988
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.35.665