A polymer based bag filter with high temperature resistance plays a key role in dust and acid gas treatment the power industry.
منابع مشابه
Synthesis and Characterization of Polyamide-66/Calcium Carbonate Composites
Polyamide-66(PA66)/CaCO3 micro- and nano-composites were prepared using a polymer solution method at filler loading of 0, 1, 2 and 3 weight percent. Nano-size of CaCO3 was synthesized by micro-emulsion technique. The material was characterized by XRD, SEM, FTIR and UV-VIS techniques. XRD results of composites suggested that CaCO3 particles are found in the amorphous phase of the semi-crystallin...
متن کاملSynthesis and Characterization of Polyamide Containing Maleimide Pendant Group
A series of new polyamides containing maleimide pendant group were prepared by low temperature polycondensation of 5-(4-(2,5-dioxo-2H-pyrrol-1(5H)-yl)benzamido)isophthaloyl chloride as a new monomer with various aromatic diamines in NMP. Monomer and polymers structures were identified through FT-IR, 1H-NMR and elemental analysis. Obtained polymers were soluble in polar solvents and non solu...
متن کاملsynthesis and characterization of polyamide-66/calcium carbonate composites
polyamide-66(pa66)/caco3 micro- and nano-composites were prepared using a polymer solution method at filler loading of 0, 1, 2 and 3 weight percent. nano-size of caco3 was synthesized by micro-emulsion technique. the material was characterized by xrd, sem, ftir and uv-vis techniques. xrd results of composites suggested that caco3 particles are found in the amorphous phase of the semi-crystallin...
متن کاملTHE OXIDATION RESISTANCE OF HIGH ALUMINUM HEAT RESISTANT STEELS
Abstract: In this research, the oxidation behaviour of high Aluminum heat resistant steel (%25Cr,%20Ni,%8Al) hasbeen evaluated at the temperature range of (1000-1300ºC).The results showed that there was no countinous healinglayer on the surface of the alloy when Al increased up to %5.5 and the oxidation resistance of steel decreased due toformation of spinel oxides on the surface.By increasing ...
متن کاملTissue engineering scaffold material of porous nanohydroxyapatite/polyamide 66
The aim of the study was to investigate a porous nanohydroxyapatite/polyamide 66 (n-HA/PA66) scaffold material that was implanted into muscle and tibiae of 16 New Zealand white rabbits to evaluate the biocompatibility and osteogenesis and osteoinductivity of the materials in vivo. The samples were harvested at 2, 4, 12 and 26 weeks respectively, and subjected to histological analysis. At 2 week...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials advances
سال: 2021
ISSN: ['2633-5409']
DOI: https://doi.org/10.1039/d1ma00420d