High-Field Torque Measurement of FePt Nanoparticles
نویسندگان
چکیده
منابع مشابه
Oxidation of FePt nanoparticles
Chemically disordered B3–7-nm-diameter FePt nanoparticles are synthesized using the airless operation technique based on decomposition of iron pentacarbonyl and reduction of platinum acetylacetonate. The particle solution is then washed and subsequently deposited onto a thermally oxidized Si substrate. Nanoparticle assemblies are formed after solvent evaporation. The samples are heat-treated us...
متن کاملMonodisperse FePt nanoparticles and ferromagnetic FePt nanocrystal superlattices
Synthesis of monodisperse iron-platinum (FePt) nanoparticles by reduction of platinum acetylacetonate and decomposition of iron pentacarbonyl in the presence of oleic acid and oleyl amine stabilizers is reported. The FePt particle composition is readily controlled, and the size is tunable from 3- to 10-nanometer diameter with a standard deviation of less than 5%. These nanoparticles self-assemb...
متن کاملStructural studies of L10 FePt nanoparticles
We have studied the lattice parameter changes of L10 FePt nanoparticles annealed to near equilibrium as a function of composition by x-ray diffraction. We have found that the ~111! diffraction peak shifts linearly with composition, however, the c parameter mostly changes in the Pt rich compositions and the a parameter mostly changes in the Fe rich compositions with respect to the equiatomic com...
متن کاملPolyol Process Synthesis of Monodispersed FePt Nanoparticles.
Monodispersed FePt nanoparticles are synthesized by reduction of iron(II) acetylacetonate and platinum(II) acetylacetonate with 1,2-hexadecanediol as the reducing reagent in the polyol process. As-prepared FePt nanoparticles are chemically disordered with fcc phase. Transmission electron microscopy (TEM) images show a self-assembled particle array with an average particle size of 3 nm and a sta...
متن کاملStructural and Magnetic Investigations on FePt Nanoparticles
Magnetic nanoparticles and thin films exhibiting a large magnetic anisotropy energy density (MAE) have attracted enormous attention over the last years due to their potential use in magnetic data storage or sensing applications. FePt alloy nanoparticles and films have a huge MAE in the chemically ordered L10 phase. This ordered phase is typically obtained by annealing the as-prepared chemically...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the Magnetics Society of Japan
سال: 2004
ISSN: 1884-6726,1346-7948
DOI: 10.3379/tmjpn2001.4.24