Growth of Perovskite Crystals from a Potassium Fluoride Flux.
نویسندگان
چکیده
منابع مشابه
Lead-flux Growth of Eu4Ir8As7 Crystals
Single crystals of the new arsenide Eu4Ir8As7 were grown from a lead flux. The structure was refined on the basis of single-crystal X-ray diffractometer data: Ca4Ir8P7 type, P21/m, a = 1311.3(1), b = 408.4(1), c = 1360.3(1) pm, β = 98.45(1)◦, wR2 = 0.0640, 1985 F2 values, 95 variables. The iridium and arsenic atoms in the Eu4Ir8As7 structure build up a complex three-dimensional, covalently bond...
متن کاملEffect of impurities on the optical properties of KTP single crystals grown from flux
In the present work, KTP crystals have been grown by spontaneous nucleation technique in flux medium using K6P4O13 flux. 0.4-1 °C/h cooling rates were applied in the spontaneous nucleation process. The presence and amount of impurities has been determined by using XRF. The optical transmission spectra of impure KTP crystals in the UV–visible region are discussed. The transmission cut-off is cle...
متن کاملMechanism for rapid growth of organic–inorganic halide perovskite crystals
Optoelectronic devices based on hybrid halide perovskites have shown remarkable progress to high performance. However, despite their apparent success, there remain many open questions about their intrinsic properties. Single crystals are often seen as the ideal platform for understanding the limits of crystalline materials, and recent reports of rapid, high-temperature crystallization of single...
متن کاملBismuth Flux Growth of CeRh6Ge4 and CeRh2Ge2 Single Crystals
Single crystals of the germanides CeRh6Ge4 and CeRh2Ge2 were synthesized from the elements in bismuth fluxes. Polycrystalline samples are available by arc-melting. The structures were refined on the basis of single-crystal X-ray diffractometer data. CeRh6Ge4: LiCo6P4 type, P6m2, a = 715.4(2), c = 385.5(1) pm, wR2 = 0.0554, 273 F2 values, 19 variables; CeRh2Ge2: ThCr2Si2 type, I4/mmm, a = 415.69...
متن کاملSynthesis of Ce2Rh3Ge5 Crystals from a Bismuth Flux
The germanide Ce2Rh3Ge5 was synthesized from the elements in a bismuth flux, and the structure was refined from single-crystal X-ray diffractometer data: U2Co3Si5 type, Ibam, a = 1010.1(2), b = 1210.4(2), c = 599.1(1) pm, wR = 0.0596, 760 structure factors, 31 variables. The rhodium and germanium atoms build up a three-dimensional [Rh3Ge5] network (242 – 269 pm Rh–Ge; 300 pm Rh–Rh; 266 pm Ge–Ge...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: NIPPON KAGAKU KAISHI
سال: 1998
ISSN: 2185-0925,0369-4577
DOI: 10.1246/nikkashi.1998.412