Flow-Velocity-Dependent Transition of Anisotropic Crack Patterns in CaCO3 Paste

نویسندگان
چکیده

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Crack Velocity Dependent Toughness in Rate Dependent Materials

Mode I, quasi-static, steady state crack growth is analyzed for rate dependent materials under plane strain conditions in small scale yielding. The solid is characterized by an elastic-viscoplastic constitutive law and the plane ahead of the crack tip is embedded with a rate dependent fracture process zone. The macroscopic work of fracture of the material is computed as a function of the crack ...

متن کامل

analyzing patterns of classroom interaction in efl classrooms in iran

با به کار گیری روش گفتما ن شنا سی در تحقیق حا ضر گفتا ر میا ن آموزگا را ن و زبا ن آموزا ن در کلا سهای زبا ن انگلیسی در ایرا ن مورد بررسی قرار گرفت. ا هداف تحقیق عبا رت بودند از: الف) شنا سا ئی سا ختارهای ارتبا ط گفتا ری میا ن معلمین و زبا ن آموزا ن ب) بررسی تا ثیر نقش جنسیت دبیرا ن و زبا ن آموزان بر سا ختا رهای ارتبا ط گفتا ری میا ن آنها پ) مشخص کردن اینکه آ یا آموزگاران غا لب بر این ارتبا ط گف...

Experimental and analytical investigation of dynamic crack patterns in automotive windshield sheets subjected to low velocity impact

Off-road cars’ windshields are vulnerable to different types of stones, road debris and pebbles due to common off paved and gravel surfaces in which they drive. Any attempt to design windshield that minimizes injury and death of occupants during a vehicle accident requires a thorough understanding of the mechanical behavior of automotive windshield subjected to foreign object impact loads...

متن کامل

Crack Propagation Speed in the Drying Process of Paste

We investigated crack propagation in the drying process of a thin layer of calcium carbonate (CaCO3) paste experimentally. Cracks are induced by uniform desiccation from the top surface of a layer at the approximately same water content for various drying conditions. We found that the crack speed is a nonlinear increasing function of the drying rate at the cracking time although the tensile str...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Journal of the Physical Society of Japan

سال: 2019

ISSN: 0031-9015,1347-4073

DOI: 10.7566/jpsj.88.024001