Fatigue strength of friction welded joints of AZ31 magnesium alloy.
نویسندگان
چکیده
منابع مشابه
Corrosion Behavior of the Friction Stir Welded AZ31 Magnesium Alloy.
* IDMEC, Instituto Superior Técnico, Universidade de Lisboa, Av. Rovisco Pais, 1049-001 Lisboa, Portugal ** DEQ/ICEMS, Instituto Superior Técnico, Universidade de Lisboa, Av. Rovisco Pais, 1049001 Lisboa, Portugal. *** Department of Engineering Design and Production, School of Engineering, Aalto University, P.O. Box 1420, FI-00076 Aalto, Finland **** Faculdade de Engenharia da universidade do P...
متن کاملevaluation of fatigue life of friction stir welded 7075-t651 aluminum alloy joints
abstract – aluminium 7075- t651 alloys are widely used in the production of light weight structures requiring a high strength to weight ratio and high corrosion resistance. the effect of processing parameters on fatigue life of 7075- t651 aluminium joints produced by friction stir welding was investigated in the present study. welding samples were made by employing rotating tool speed of 770, 9...
متن کاملFatigue of Friction Stir Welded 2024-T351 Aluminium Alloy
Fatigue failure characteristics of friction stir welds in 13mm gauge 2024-T351 plate have been assessed. Failure occurred from either the weld region (nugget/flow arm) or from the material immediately surrounding the weld. Fatigue failure from the surrounding material was essentially conventional, initiating from large S-phase intermetallic particles and growing in a macroscopic mode I manner. ...
متن کاملThe effect of Zn element addition on dissimilar Al6061/AZ31 friction stir welded joints
In this study, friction stir butt welding of Mg and Al alloys with applying Zn interlayer was performed. To obtain optimum condition, a combination of two travel and three rotation speeds were selected. Mg-Zn and Mg-Al-Zn IMCs, Al solid solution and residual Zn, were the most common phases in the stirred zone, which eliminated the formation of Al-Mg intermetallics. The maximum mechanical proper...
متن کاملImproving Fatigue Strength of Welded Joints by Ultrasonic Impact Treatment
Enhancement in fatigue performance of welded joints by Ultrasonic Impact Treatment (UIT) was evaluated with large-scale rolled beam and built-up specimens having yield strength of 345 to 760 MPa. Eighteen rolled-beam specimens having welded details at cover plates and transverse stiffeners and eight built-up specimens having only transverse stiffener details were fatigue tested after treating t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Japan Institute of Light Metals
سال: 1994
ISSN: 0451-5994
DOI: 10.2464/jilm.44.147