FATIGUE STRENGTH OF CORRODED GALVANIZED STEEL WIRES
نویسندگان
چکیده
منابع مشابه
Influence of the Manufacturing Process on Defects in the Galvanized Coating of High Carbon Steel Wires
This study is a detailed failure analysis of galvanized high carbon steel wires, which developed coating cracks during the torsion test performed as a quality control at the end of the manufacturing process. Careful visual inspections showed that the cracks are already present in the coating before the torsion test. In order to explain the origin of these cracks, systematic metallographic inves...
متن کاملCorrosion of Galvanized Steel in Soils
The results of measurements of the corrosion of galvanized steel and of bare steel and zinc as reference materials after exposure to different soil conditions for a maximum of 13 years are reported. The magnitude and progress of corrosion of galvanized steel as determined by weight loss and pitting is interpreted in terms of the environmental conditions to which the specimens were exposed. From...
متن کاملReal-time monitoring of laser welding of galvanized high strength steel in lap joint configuration
Two different cases regarding the zinc coating at the lap joint faying surface are selected for studying the influence of zinc vapor on the keyhole dynamics of the weld pool and the final welding quality. One case has the zinc coating fully removed at the faying surface; while the other case retains the zinc coating on the faying surface. It is found that removal of the zinc coating at the fayi...
متن کاملFatigue Properties of the Ultra-High Strength Steel TM210A
This paper presents the results of an experiment to investigate the high cycle fatigue properties of the ultra-high strength steel TM210A. A constant amplitude rotating bending fatigue experiment was performed at room temperature at stress ratio R = -1. In order to evaluate the notch effect, the fatigue experiment was carried out upon two sets of specimens, smooth and notched, respectively. In ...
متن کاملNotch fatigue behavior: Metallic glass versus ultra-high strength steel
Studying the effect of notch on the fatigue behavior of structural materials is of significance for the reliability and safety designing of engineering structural components. In this work, we conducted notch fatigue experiments of two high-strength materials, i.e. a Ti32.8Zr30.2Ni5.3Cu9Be22.7 metallic glass (MG) and a 00Ni18Co15Mo8Ti ultra-high strength steel (CM400 UHSS), and compared their no...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Doboku Gakkai Ronbunshuu A
سال: 2006
ISSN: 1880-6023
DOI: 10.2208/jsceja.62.614