Fatigue Strength and Fracture Mechanisms of WC Cermet-Sprayed Steel.
نویسندگان
چکیده
منابع مشابه
FRACTURE AND FATIGUE BEHAVIOR OF WC-Co AND WC-CoNi CEMENTED CARBIDES
The fracture and fatigue characteristics of several cemented carbide grades are investigated as a function of their microstructure. In doing so, the influence of binder chemical nature and content (Co and 76wt%Co-24wt%Ni), as well as carbide grain size on hardness, flexural strength, fracture toughness and fatigue crack growth (FCG) behavior is evaluated. Mechanical testing is combined with a d...
متن کاملEffect of WC Concentration on Abrasive Wear Properties of the Thermally Sprayed WC -Ni Coatings
In this work the effects of WC concentration on abrasive wear behavior by thermally sprayed WC coating was evaluated using three body abrasive wear tester. A different combination of WC and NI coatings were deposited on steel substrates by flame spraying using powder with different WC concentrations (0 %, 12.5 %, 25 %, and 50 %). Flame torch was used for heating and coating of process. Microstr...
متن کاملEffect of Surface Roughness Morphology on Bond Strength of Thermal Sprayed WC-10Co-4Cr Ceramic/Metal Coating
In this study, the effect of surface roughness and roughness morphology on the bond strength of WC-Co-Cr coatings has investigated. The three different surfaces morphology are use for this purpose. The first and tow samples sandblasted with alumina and silicon carbide respectively. Other sample no sandblasted before spraying process. The same WC-10Co-4Cr coating deposited on the substrates with...
متن کاملFatigue Failure of Structural Steel – Analysis Using Fracture Mechanics
Fatigue is the major threat in service of steel structure subjected to fluctuating loads. With the additional effect of corrosion and presence of weld joints the fatigue failure may become more critical in structural steel. One of the apt examples of such structural is the sailing ship. This is experiencing a constant stress due to floating and a pulsating bending load due to the waves. This pa...
متن کاملFatigue Properties of the Ultra-High Strength Steel TM210A
This paper presents the results of an experiment to investigate the high cycle fatigue properties of the ultra-high strength steel TM210A. A constant amplitude rotating bending fatigue experiment was performed at room temperature at stress ratio R = -1. In order to evaluate the notch effect, the fatigue experiment was carried out upon two sets of specimens, smooth and notched, respectively. In ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1996
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.45.927