Fatigue Properties of Fillet Welded Joints on Piping System.
نویسندگان
چکیده
منابع مشابه
The Fatigue Strength of Fillet Welded Connections
This report describes a study of the fatigue behavior of fillet welded joints stressed perpendicular to the weld line. The study included an experimental phase in which the stiess-life and cracking behavior of load and nonload carrying fillet weld joints was determined. This experimental study concentrated on the fatigue behavior in the transition region between high and low cycle fatigue 3 5 (...
متن کاملFatigue Behaviour Study of Laser Hybrid Welded Eccentric Fillet Joints – Part Ii: State-of-the-art of Fracture Mechanics and Fatigue Analysis of Welded Joints
Simplified fatigue and fracture mechanics based assessment methods are widely used by the industry to determine the structural integrity significance of postulated cracks, manufacturing flaws, service-induced cracking or suspected degradation of engineering components under normal and abnormal service loads. In many cases, welded joints are the regions most likely to contain original fabricatio...
متن کاملFatigue Behaviour Study of Laser Hybrid Welded Eccentric Fillet Joints – Part I
Welded joints are a major component that is often responsible for causing a structure failure or for being the point at which fatigue cracking initiates and propagates. Despite tremendous research efforts, the understanding of fatigue behaviour is still limited, particularly for new techniques like laser hybrid welding. Beside a comprehensive state-of-the-art study, the paper presents a fatigue...
متن کاملFatigue Life of Repaired Welded Tubular Joints
In this study, the effect of repair on fatigue life of tubular joints is investigated. Six cracked specimens precedently subjected to fatigue loading undergone to weld repair. Two of those specimens were shot peened before primary fatigue loading. It is shown that repair gives rise to about 150% increase in fatigue life for original specimens while the increase of fatigue life for shot-peened ...
متن کاملFatigue Strength of Fillet-Welded Transverse Stiffeners with Undercuts
Presently, wrapping of the welds at the ends of stiffeners is not done to avoid the undercutting of the stiffener corners and the attendant weld repair. The fatigue performance of stiffeners with undercuts was evaluated in a factorial design fatigue experiment. Undercuts at the flange edge and filling of the stiffener cope with the fillet weld were also evaluated. The undercuts did not influenc...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY
سال: 1993
ISSN: 0288-4771
DOI: 10.2207/qjjws.11.180