Fabrication of Alumina Nanofibers via Anodizing and Its Surface Functionalization
نویسندگان
چکیده
منابع مشابه
Ultra-High Density Single Nanometer-Scale Anodic Alumina Nanofibers Fabricated by Pyrophosphoric Acid Anodizing
Anodic oxide fabricated by anodizing has been widely used for nanostructural engineering, but the nanomorphology is limited to only two oxides: anodic barrier and porous oxides. Therefore, the discovery of an additional anodic oxide with a unique nanofeature would expand the applicability of anodizing. Here we demonstrate the fabrication of a third-generation anodic oxide, specifically, anodic ...
متن کاملFabrication of transparent alumina (Al2O3) nanofibers by electrospinning
Transparent alumina nanofibers have been fabricated from a suitable inorganic–organic composite solution by spinning in an electric field (strength 70–90 kV/m) applied between the tip of a needle and the target plate. Upon firing and sintering under carefully pre-selected time–temperature rofiles (heating rate, temperature and soak time), high-purity and crystalline alumina nanofibers retaining...
متن کاملCharacterization and application of electrospun alumina nanofibers
Alumina nanofibers were prepared by a technique that combined the sol-gel and electrospinning methods. The solution to be electrospun was prepared by mixing aluminum isopropoxide (AIP) in ethanol, which was then refluxed in the presence of an acid catalyst and polyvinylpyrolidone (PVP) in ethanol. The characterization results showed that alumina nanofibers with diameters in the range of 102 to ...
متن کاملRapid fabrication of self-ordered porous alumina with 10-/sub-10-nm-scale nanostructures by selenic acid anodizing
Anodic porous alumina has been widely investigated and used as a nanostructure template in various nanoapplications. The porous structure consists of numerous hexagonal cells perpendicular to the aluminum substrate and each cell has several tens or hundreds of nanoscale pores at its center. Because the nanomorphology of anodic porous alumina is limited by the electrolyte during anodizing, the d...
متن کاملPreparation and Characterization of High Specific Surface Area γ-Alumina Nanoparticles Via Sol-Gel Method
In the present investigation, γ-alumina nanoparticles with particle sizes less than 10 nm, high specific surface area (351 m2/g), high pore volumes and relatively narrow pore sizes distribution was prepared via sol-gel method in presence of aluminum isopropoxide as an aluminum precursor, distilled water, acetic acid as hydrolysis rate controller and tert-butanol as solvent. They had meso ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of The Surface Finishing Society of Japan
سال: 2016
ISSN: 0915-1869,1884-3409
DOI: 10.4139/sfj.67.527