Experimental study of emergent ground state behavior in Gd<sub>1-x</sub>Ce<sub>x</sub>Ni<sub>5</sub> (x = 0; 0.2; 0.5; 0.8 and 1) melt-spun ribbons
نویسندگان
چکیده
The ground state physical properties of Gd 1-x Ce x Ni 5 (x = 0; 0.2; 0.5; 0.8 and 1) melt-spun ribbons were investigated by X-ray diffraction, magnetization specific heat measurements. produced ribbon samples are single phases with the hexagonal CaCu -type crystal structure. magnetic transition temperature decreases increasing content. At a around 100 K for CeNi ribbon, spin fluctuations effect is visible.
منابع مشابه
Effect of Joule-Heating Annealing on Giant Magnetoimpedance of Co64Fe4Ni2B19-xSi8Cr3Alx (x = 0, 1 and 2) Melt-Spun Ribbons
In this work, we have studied the influence of dc joule-heating thermal processing on the structure, magnetoimpedance (MI) and thermal properties of Co64Fe4Ni2B19-xSi8Cr3Alx (x = 0, 1, and 2) rapidly solidified melt-spun ribbons. The nanocrystallization process was carried out by the current annealing of as-spun samples at various current densities. As-spun and joule-heated samples were studied...
متن کاملPhase transition and magnetocaloric properties of Mn50Ni42−xCoxSn8 (0 ≤ x ≤ 10) melt-spun ribbons
The characteristics of magnetostructural coupling play a crucial role in the magnetic field-driven behaviour of magnetofunctional alloys. The availability of magnetostructural coupling over a broad temperature range is of great significance for scientific and technological purposes. This work demonstrates that strong magnetostrucural coupling can be achieved over a wide temperature range (222 t...
متن کاملThe Structure and Magnetic Properties of Co77Zr18W5 Melt-Spun Ribbons
Based on X-ray diffraction, microscopic and magnetic analysis, the structure and magnetic properties of Co77Zr18W5 melt-spun ribbons were studied in this paper. A new element to stabilize the metastable Co5Zr phase was found and the coercivity observed in Co-Zr alloys can be obviously enhanced by proper tungsten substitution. The Curie temperature of Co77Zr18W5 ribbons is 475 ̊C which suggests t...
متن کاملShapes of the Icosahedral Quasicrystalline Phase in Melt-spun Ribbons
T. Bončina, University of Maribor, Faculty of Mechanical Engineering, Maribor, Slovenia The shapes of icosahedral quasicrystalline (IQC) particles were determined in melt-spun ribbons of alloys based on the Al-Mn-Be alloy system. The sizes of the quasicrystalline particles ranged from a few tenths of nanometres up to 1 μm. Therefore, diff erent methods were employed for characterizing their sha...
متن کاملDip coating of silica layer on melt-spun Finemet ribbons: surface morphology and electrical resistivity changes
In this study, melt-spun Finemet ribbons were coated by a thin layer of SiO2 using dip coating method. Amorphous ribbon prepared by melt spinning method and dip coating were done by using a solution of tetraethylen orthosilicate as a SiO2 precursor, ethanol as solvent and distilled water for hydrolysis. Different thicknesses of SiO2 layer, namely 304, 349, 451, 526 and 970 nm were obtained prop...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: AIP Advances
سال: 2022
ISSN: ['2158-3226']
DOI: https://doi.org/10.1063/9.0000277